热处理对N80钢表面镍基合金涂层CO2腐蚀性能的影响
Effect of Heat Treatment on CO2 Corrosion Resistance of Ni-based Alloy Coating on N80 Steel
摘 要
利用等离子热喷涂技术在N80钢表面制备了镍基合金涂层, 并进行高温扩散处理。通过CO2高温高压腐蚀试验评价涂层在模拟油田环境中的耐蚀性能, 利用扫描电镜(SEM)、X射线衍射(XRD)方法分析了涂层的微观形貌和相组成。结果表明, 镍基合金涂层由单质Ni相及固溶体Cr1.2Ni2.88、FeNi3、MoO2和CuO组成。经过600 ℃扩散处理后, 涂层内原子结构更为致密。涂层的CO2高温高压腐蚀速率为0.0046 mm/a, 是原始涂层的1/100, 具有优良的抗CO2高温高压腐蚀性能。
镍基合金涂层
CO2腐蚀
N80 steel
Ni-based alloy coating
CO2 corrosion
Abstract
Ni-based alloy coating was made on N80 steel substrate by plasma arc spraying, and then high temperature diffusion process was performed. The CO2 corrosion properties of the Ni-based alloy coating in simulated oil field environment were tested. The microstructure and phase constituents of the coating were analyzed by SEM, EDX and XRD. The results show that the phase constituents of the Ni-based alloy coating were Ni, Cr1.2Ni2.88, FeNi3、MoO2 and CuO. After heat treatment at 600 ℃ for 1 h, the coating was denser. The CO2 corrosion rate of the coating after heat treatment was 0.0046 mm/a, and was about 1/100 of the coating before heat treatment. The coating after heat treatment had excellent CO2 corrosion resistance.
中图分类号 TG172.8 TG174.44
所属栏目 试验研究
基金项目 陕西省科学技术研究发展计划项目(No.2008K01-31)
收稿日期 2011/5/9
修改稿日期
网络出版日期
作者单位点击查看
备注吴向清, 副教授, 博士,
引用该论文: WU Xiang-qing,XIE Fa-qin,SUN Can,TIAN Wei. Effect of Heat Treatment on CO2 Corrosion Resistance of Ni-based Alloy Coating on N80 Steel[J]. Corrosion & Protection, 2012, 33(3): 190
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙海礁, 叶帆. 塔河油田油套管内壁的腐蚀与防护[J]. 腐蚀与防护, 2010, 31(5):383-386.
【2】张学元, 邸超, 雷良才. 二氧化碳腐蚀与控制[M]. 北京:化学工业出版社, 2000.
【3】Kerman M B, Morshed A. Carbon dioxide corrosion in oil gas production-a compendium critical review of corrosion science and engineering[J]. Corrosion, 2003, 59(8):659-683.
【4】李国敏, 李爱魁, 郭兴蓬, 等. 油气田开发中的CO2腐蚀及防护技术[J]. 材料保护, 2003, 36(6):1-5.
【5】路民旭, 白真权, 赵新伟, 等. 油气采集储运中的腐蚀现状及典型案例[J].腐蚀与防护, 2003, 23(3):105-113.
【6】林冠发, 白真权, 赵国仙, 等. CO2压力对金属腐蚀产物膜形貌结构的影响[J].中国腐蚀与防护学报, 2004, 24(5):284-288.
【7】龙媛媛, 许卫国, 张洁, 等. 钨基非晶合金镀层对油套管用钢的防蚀阻垢性能[J].腐蚀与防护, 2010, 31(4):316-317.
【8】尤郭群, 李春福, 任海, 等. N80钢化学镀Ni-Fe-P的抗CO2腐蚀性能研究[J].化工时刊, 2008, 22(5):20-22.
【2】张学元, 邸超, 雷良才. 二氧化碳腐蚀与控制[M]. 北京:化学工业出版社, 2000.
【3】Kerman M B, Morshed A. Carbon dioxide corrosion in oil gas production-a compendium critical review of corrosion science and engineering[J]. Corrosion, 2003, 59(8):659-683.
【4】李国敏, 李爱魁, 郭兴蓬, 等. 油气田开发中的CO2腐蚀及防护技术[J]. 材料保护, 2003, 36(6):1-5.
【5】路民旭, 白真权, 赵新伟, 等. 油气采集储运中的腐蚀现状及典型案例[J].腐蚀与防护, 2003, 23(3):105-113.
【6】林冠发, 白真权, 赵国仙, 等. CO2压力对金属腐蚀产物膜形貌结构的影响[J].中国腐蚀与防护学报, 2004, 24(5):284-288.
【7】龙媛媛, 许卫国, 张洁, 等. 钨基非晶合金镀层对油套管用钢的防蚀阻垢性能[J].腐蚀与防护, 2010, 31(4):316-317.
【8】尤郭群, 李春福, 任海, 等. N80钢化学镀Ni-Fe-P的抗CO2腐蚀性能研究[J].化工时刊, 2008, 22(5):20-22.
相关信息