咪唑啉缓蚀剂对减粘塔塔顶流出系统的缓蚀作用
Effect of Imidazoline Inhibitor Used in Outflow System of Tower Processing Thick Oil
摘 要
通过对腐蚀介质的气相色谱分析和腐蚀产物的XRD分析, 研究了辽河某炼油厂稠油加工减粘塔塔顶系统的腐蚀机理; 采用电化学法和静态挂片法研究了20钢在加入咪唑啉缓蚀剂的腐蚀介质中的缓蚀作用。结果表明, 20钢试样在减粘塔顶水介质中发生了显著的低温HCl+H2S+H2O腐蚀; A1缓蚀剂主要成分为咪唑啉, 属阳极吸附性缓蚀剂, 可在20号钢表面形成一层高阻值疏水性保护膜, 最佳缓蚀剂添加浓度为100 mg/L时, 缓蚀率最大为84%。
缓蚀剂
电化学方法
缓蚀机理
low temperature sulfur corrosion
corrosion inhibitor
electrochemical method
corrosion mechanism
Abstract
The corrosion mechanism of overhead system of visbreaking tower of a refinery in Liaohe was studied by gas chromatography of corrosion media and XRD of corrosion products. The corrosion inhibitor for 20 steel in the corrosion media was studied by static weigt loss method and electrochemical polarization curves. The results showed that 20 steel samples in the water medium in the top of the visbreaking tower suffered low temperature HCl + H2S +H2O corrosion markedly. The main ingredient of A1 corrosion inhibitor is imidazoline. Al is an anodic corrosion inhibitor which can form hydrophobic protective layer on the surface of 20 steel. When the best concentration of A1 was 100 mg/L the inhibition efficiency was 84%.
中图分类号 TG174.42 TE986
所属栏目 试验研究
基金项目
收稿日期 2011/9/13
修改稿日期
网络出版日期
作者单位点击查看
备注唐静, 硕士研究生,
引用该论文: TANG Jing,ZHANG Guo-fu,SHI Yan-hua,LIANG Ping. Effect of Imidazoline Inhibitor Used in Outflow System of Tower Processing Thick Oil[J]. Corrosion & Protection, 2012, 33(5): 411
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】崔波, 石文平, 戴树, 等. 高粘度稠油开采方法的现状与研究进展[J]. 石油化工技术经济, 2000, 16(6):5-10.
【2】左慧君, 刘吟, 阳光, 等. 稠油加工装置的腐蚀与防护[J]. 全面腐蚀控制, 2007, 21(4):38-41.
【3】杨同莲. 常减压装置高硫油加工的腐蚀与防护[J]. 化工设备与管道, 2005, 42(4):47-49.
【4】黄永章, 程刚, 冯东红, 等. 加工苏丹稠油减黏裂化装置的腐蚀[J]. 石油化工腐蚀与防护, 2007, 24(6):30-32.
【5】李庆梅, 丛培振, 刘明辉. 炼油厂常压蒸馏工艺防腐蚀优化[J]. 腐蚀与防护, 2004, 25(5):219-220.
【6】朱镭, 于萍, 罗运柏. 咪唑啉缓蚀剂的研究与应用进展[J]. 材料保护, 2003, 36(12):4-7.
【7】傅晓萍. 蒸馏装置塔顶缓蚀剂技术现状[J]. 石油化工腐蚀与防护, 2005, 22(2):15-18.
【8】Mahmoud S S. Corrosion inhibition of iron by amphoteric surfactants in hydrochloric acid solutions[J]. J Mater Sci, 2007, 42:989-997.
【9】Raja Pandian Bothi, Rahim Afidah Abdul, Osman Hasnah, et al. Inhibitory effect of kopsia singapurensis extract on the corrosion behavior of mild steel in acid media[J]. Acta Phys Chim Sin, 2010, 26(8):2171-217.
【10】Chaiebe, Bouyanzer A, Hammoutib. Limonene as green inhibitor for steel corrosion in hydrochloric scid solutions[J]. Acta Phys Chim Sin, 2009, 25(7):1254-1258.
【11】阮晓刚, 杨启明, 刘清友. 加工稠油的常压装置的腐蚀机理分析[J]. 炼油技术与工程, 2005, 35(5):15-16.
【12】郭睿, 吴从华, 左笑, 等. 一种复合型咪唑啉缓蚀剂[J]. 腐蚀与防护, 2006, 27(7):341-343.
【13】雷良才, 肖恺, 沈愚, 等. 咪唑啉缓蚀剂的合成与缓蚀性能研究[J]. 腐蚀与防护, 2001, 22(10):430-432.
【2】左慧君, 刘吟, 阳光, 等. 稠油加工装置的腐蚀与防护[J]. 全面腐蚀控制, 2007, 21(4):38-41.
【3】杨同莲. 常减压装置高硫油加工的腐蚀与防护[J]. 化工设备与管道, 2005, 42(4):47-49.
【4】黄永章, 程刚, 冯东红, 等. 加工苏丹稠油减黏裂化装置的腐蚀[J]. 石油化工腐蚀与防护, 2007, 24(6):30-32.
【5】李庆梅, 丛培振, 刘明辉. 炼油厂常压蒸馏工艺防腐蚀优化[J]. 腐蚀与防护, 2004, 25(5):219-220.
【6】朱镭, 于萍, 罗运柏. 咪唑啉缓蚀剂的研究与应用进展[J]. 材料保护, 2003, 36(12):4-7.
【7】傅晓萍. 蒸馏装置塔顶缓蚀剂技术现状[J]. 石油化工腐蚀与防护, 2005, 22(2):15-18.
【8】Mahmoud S S. Corrosion inhibition of iron by amphoteric surfactants in hydrochloric acid solutions[J]. J Mater Sci, 2007, 42:989-997.
【9】Raja Pandian Bothi, Rahim Afidah Abdul, Osman Hasnah, et al. Inhibitory effect of kopsia singapurensis extract on the corrosion behavior of mild steel in acid media[J]. Acta Phys Chim Sin, 2010, 26(8):2171-217.
【10】Chaiebe, Bouyanzer A, Hammoutib. Limonene as green inhibitor for steel corrosion in hydrochloric scid solutions[J]. Acta Phys Chim Sin, 2009, 25(7):1254-1258.
【11】阮晓刚, 杨启明, 刘清友. 加工稠油的常压装置的腐蚀机理分析[J]. 炼油技术与工程, 2005, 35(5):15-16.
【12】郭睿, 吴从华, 左笑, 等. 一种复合型咪唑啉缓蚀剂[J]. 腐蚀与防护, 2006, 27(7):341-343.
【13】雷良才, 肖恺, 沈愚, 等. 咪唑啉缓蚀剂的合成与缓蚀性能研究[J]. 腐蚀与防护, 2001, 22(10):430-432.
相关信息