Analysis of Stress Corrosion Cracking of Beryllium Bronze Spring Flake
摘 要
微动开关的弹簧片在使用过程中发生开裂。对弹簧片进行了裂纹形貌观察、能谱成分分析、金相组织检查和硬度检测, 并对完好弹簧片进行了模拟试验。结果表明, 弹簧片裂纹为应力腐蚀开裂; 造成弹簧片应力腐蚀开裂的腐蚀介质来源于微动开关长接触片及传感器插座焊点部位残留的氯化铵钎剂。通过采用氯化锌+甘油替代含氯化铵的钎剂, 弹簧片的应力腐蚀开裂得到了有效预防。
Abstract
The spring flake of a sensitive switch cracked during working. Appearance observation, energy spectrum analysis, microstructure inspection and hardness testing were performed. Then simulated testing for intact spring flake was carried out. The results show that the crack of spring flake is stress corrosion crack. The corrosion medium derived from the remaining flux containing NH4Cl at the welding point belween long contact flake and socket. By using ZnCl2 and glycerin to substitute as flux containing NH4Cl, the cracking of the spring flake has been effectively prevented.
中图分类号 TG172.6
所属栏目 失效分析
基金项目
收稿日期 2011/8/26
修改稿日期
网络出版日期
作者单位点击查看
备注刘德林, 博士研究生,
引用该论文: LIU De-lin,LI Chun-guang,TAO Chun-hu,HE Yu-huai,LI Ying. Analysis of Stress Corrosion Cracking of Beryllium Bronze Spring Flake[J]. Corrosion & Protection, 2012, 33(5): 452
被引情况:
【1】王裕林,唐海军,李 飞,杨秀锋, "某型直升机尾梁蒙皮开裂的失效分析",腐蚀与防护 37, 1026-1029(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄伯云, 李成功, 石力开, 等. 中国材料工程大典. 第4卷, 有色金属材料工程[M]. 北京:化学工业出版社, 2005:274-275.
【2】重有色金属材料加工手册编写组. 重有色金属材料加工手册第一分册[M]. 北京:冶金工业出版社, 1979:204-205.
【3】张栋, 钟培道, 陶春虎, 等. 失效分析[M]. 北京:国防工业出版社, 2004:192-193.
【4】马远征. 循环蒸发器产生裂纹的原因分析[J]. 浙江化工, 2005, 36(7):41-42.
【5】王吉会, 姜晓霞, 李曙, 等. 腐蚀磨损过程中材料的环境脆性[J]. 材料研究学报, 2003, 17(5):454-455.
【6】姜涛, 于洋, 杨胜, 等. 从失效案例探讨不锈钢的应力腐蚀问题[J]. 腐蚀与防护, 2011, 32(4):297-300.
【2】重有色金属材料加工手册编写组. 重有色金属材料加工手册第一分册[M]. 北京:冶金工业出版社, 1979:204-205.
【3】张栋, 钟培道, 陶春虎, 等. 失效分析[M]. 北京:国防工业出版社, 2004:192-193.
【4】马远征. 循环蒸发器产生裂纹的原因分析[J]. 浙江化工, 2005, 36(7):41-42.
【5】王吉会, 姜晓霞, 李曙, 等. 腐蚀磨损过程中材料的环境脆性[J]. 材料研究学报, 2003, 17(5):454-455.
【6】姜涛, 于洋, 杨胜, 等. 从失效案例探讨不锈钢的应力腐蚀问题[J]. 腐蚀与防护, 2011, 32(4):297-300.
相关信息