镀锌层三价铬黑色钝化膜的耐蚀性能
Corrosion Resistance of Trivalent Chromium Black Passive Film on Zinc Coating
摘 要
制备了一种环保、不含六价铬的三价铬黑色钝化液, 选择适当的封闭剂, 研究其在镀锌层表面钝化后的耐腐蚀性能。通过醋酸铅点滴试验、塔菲尔极化曲线测试、电化学阻抗测试检测钝化膜的耐蚀性及采用扫描电子显微镜观察其表面形貌。结果表明: 镀锌层表面经三价铬黑色钝化后再进行封闭处理, 弥补了Cr3+钝化后无自愈能力的缺点, 显著提高了镀锌层钝化膜的耐腐蚀性能,而且达到了Cr6+黑色钝化的外观效果。
三价铬
黑色钝化
耐蚀性
自愈能力
galvanizing
trivalent chromium
black passivation
anti-corrosion property
self-healing ability
Abstract
An environmental friendly trivalent chromium passivation solution without Cr6+ was prepared and a suitable sealing for the solution was choosed to study corrosion resistance of the passive film on galvanized steel sheet formed in this solution. The anti-corrosion property and morphology of the passive film were analyzed by Pb(CH3COO)2 solution spot test, tafel polarization curves, EIS and scanning electron microscopy. The results indicate that the obtained black passive film not only had an appearanced as good as that after Cr6+treatment but also complemented the problem without self-healing ability for the Cr3+ passivation. The corrosion resistance can be increased significantly after treatment with sealant.
中图分类号 TG178
所属栏目 应用技术
基金项目
收稿日期 2011/7/27
修改稿日期
网络出版日期
作者单位点击查看
备注柯昌美,教授,博士,
引用该论文: KE Chang-mei,ZHOU Li-qin,WANG Zhen-zhong,ZHANG Jin-long,WANG Qian,ZHANG Li-yu,CHEN Hong-xiang. Corrosion Resistance of Trivalent Chromium Black Passive Film on Zinc Coating[J]. Corrosion & Protection, 2012, 33(6): 535
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Gigandet M P,Faucheu J,Tachez M. Formation of black chromate conversion coating on pure and zinc alloy electrolytic deposits:role of the main constituens[J]. Surface and Coating Technology,1997,89(3),285-291.
【2】余祖孝, 梁鹏飞, 孙贤, 等. 添加剂对镀锌层三价铬钝化膜耐蚀性能的影响[J]. 腐蚀与防护,2008,29(6):319-321.
【3】朱立群,杨飞. 环保型镀锌层蓝色钝化膜耐腐蚀性能的研究[J]. 腐蚀与防护,2006,27(10):503-507.
【4】朱瑞鑫. 镀锌黑色钝化工艺研究及生产中的应用[J]. 表面技术,1994,23(6):278-281.
【5】沈品华, 屠振密. 电镀锌及锌合金[M]. 北京, 机械工业出版社, 2002.
【6】Bellezze T,Roventi G,Fratesi R. Electrochemical study on the corrosion resistance of Cr3+-based conversion layers on zinc coatings[J]. Surface and Coating Technology,2002,155:221-230.
【7】Camila Boin. Black passivation films without hexavalent chromium on top of electroplated layers of zinc and zinc alloys[EB/OL]. Http://www.surtec.com/articles.html,2007-01.
【8】陈笃慧, 陈声培, 叶世源. 锌黑色钝化膜的组成及其形成机理[J]. 厦门大学学报: 自然科学版, 1987,26(4):456-461.
【9】尚定书. 镀锌层的黑色钝化[J]. 电镀与精饰, 2000,22(1):28-30.
【10】孙文军. 镀锌黑钝化[J]. 电镀与环保, 1997,17(1):36.
【11】沈品华. 镀锌三价铬钝化[J]. 电镀与环保, 2007,27(3):27-30.
【12】毕四富. 镀锌层三价铬黑色钝化工艺的研究[J]. 电镀与环保, 2007,27(4):17-20.
【13】叶金堆. 新型三价铬钝化技术[J]. 电镀与涂饰, 2006,25(7):40-43.
【14】张景双, 沈水云, 杨国强, 等. 镀锌层三价铬彩色钝化工艺的研究[J]. 电镀与环保, 2007,27(2):28-31.
【15】郑环宇, 安茂忠, 范立双. Zn-Ni合金镀层的黑色钝化工艺研究[J]. 电镀与涂饰, 2005,24(4):10-13.
【16】牟世辉. 添加剂对电镀锌层烷氧基硅烷钝化膜电化学行为的影响[J]. 表面技术, 2009,38(3):23-24,82.
【17】林子丰, Bjrn Dingwerth. 新三价铬黑色钝化的后浸处理——第二钝化层[J]. 电镀与涂饰, 2008,27(7): 21-25.
【2】余祖孝, 梁鹏飞, 孙贤, 等. 添加剂对镀锌层三价铬钝化膜耐蚀性能的影响[J]. 腐蚀与防护,2008,29(6):319-321.
【3】朱立群,杨飞. 环保型镀锌层蓝色钝化膜耐腐蚀性能的研究[J]. 腐蚀与防护,2006,27(10):503-507.
【4】朱瑞鑫. 镀锌黑色钝化工艺研究及生产中的应用[J]. 表面技术,1994,23(6):278-281.
【5】沈品华, 屠振密. 电镀锌及锌合金[M]. 北京, 机械工业出版社, 2002.
【6】Bellezze T,Roventi G,Fratesi R. Electrochemical study on the corrosion resistance of Cr3+-based conversion layers on zinc coatings[J]. Surface and Coating Technology,2002,155:221-230.
【7】Camila Boin. Black passivation films without hexavalent chromium on top of electroplated layers of zinc and zinc alloys[EB/OL]. Http://www.surtec.com/articles.html,2007-01.
【8】陈笃慧, 陈声培, 叶世源. 锌黑色钝化膜的组成及其形成机理[J]. 厦门大学学报: 自然科学版, 1987,26(4):456-461.
【9】尚定书. 镀锌层的黑色钝化[J]. 电镀与精饰, 2000,22(1):28-30.
【10】孙文军. 镀锌黑钝化[J]. 电镀与环保, 1997,17(1):36.
【11】沈品华. 镀锌三价铬钝化[J]. 电镀与环保, 2007,27(3):27-30.
【12】毕四富. 镀锌层三价铬黑色钝化工艺的研究[J]. 电镀与环保, 2007,27(4):17-20.
【13】叶金堆. 新型三价铬钝化技术[J]. 电镀与涂饰, 2006,25(7):40-43.
【14】张景双, 沈水云, 杨国强, 等. 镀锌层三价铬彩色钝化工艺的研究[J]. 电镀与环保, 2007,27(2):28-31.
【15】郑环宇, 安茂忠, 范立双. Zn-Ni合金镀层的黑色钝化工艺研究[J]. 电镀与涂饰, 2005,24(4):10-13.
【16】牟世辉. 添加剂对电镀锌层烷氧基硅烷钝化膜电化学行为的影响[J]. 表面技术, 2009,38(3):23-24,82.
【17】林子丰, Bjrn Dingwerth. 新三价铬黑色钝化的后浸处理——第二钝化层[J]. 电镀与涂饰, 2008,27(7): 21-25.
相关信息