固溶处理温度对304奥氏体不锈钢敏化与晶间腐蚀的影响
Influence of Solution Treatment Temperature on Sensitization of 304 Austenitic Stainless Steel
摘 要
采用电化学动电位再活化法(EPR)研究了经950 ℃和1050 ℃固溶处理304奥氏体不锈钢晶间腐蚀敏化度Ir/Ia、敏化时间t和敏化温度T之间关系, 根据腐蚀速率Rmpy与微观腐蚀形貌绘制了304不锈钢敏化的TTS曲线, 探讨了固溶处理温度改变对TTS曲线的影响。结果表明, 1050 ℃固溶处理试样的耐晶间腐蚀性能优于950 ℃固溶处理试样。
固溶处理
敏化处理
晶间腐蚀
电化学动电位再活化法(EPR)
304 austenitic stainless steel
solution treatment
sensitization
intergranular corrosion
electrochemical potentiodynamic reactivati(EPR)
Abstract
By means of electrochemical potentiodynamic reactivation(EPR) method the relationship among the sensitization degree(Ir/Ia), sensitization time(t) and sensitization temperature(T) of austenitic stainless steel after solution at 950 ℃ and 1050 ℃ was studied. According to the corrossion rate R and corresponding micro corrosion morphology, the related Rmpy -T-t was plotted and the influence of solid-solution treatment temperature on TTS curve was discussed . The intergranular corrosion resistance of the samples soluted at 1050 ℃ was better than those soluted at 950 ℃.
中图分类号 TG172
所属栏目 试验研究
基金项目
收稿日期 2011/9/1
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Gen-yuan,WU Qing-fei. Influence of Solution Treatment Temperature on Sensitization of 304 Austenitic Stainless Steel[J]. Corrosion & Protection, 2012, 33(8): 695
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】肖纪美. 不锈钢的金属学问题[M]. 北京:冶金工业出版社, 1983:210-224.
【2】李长荣, 张维敬, 张文奇. 奥氏体不锈钢敏化动力学过程模拟[J]. 中国腐蚀与防护学报, 1989, 9(4):249-260.
【3】Sourmail T, Too C H, Bhadeshia H K D H. Sensitization and evolution of chromium depleted zones in Fe-Cr-Ni-C systems[J]. ISIJ International, 2003, 43:1814-1820.
【4】金维松, 郎宇平, 荣凡, 等. EPR法评价奥氏体不锈钢晶间腐蚀敏感性的研究[J]. 中国腐蚀与防护学报, 2007, 27(1):54-59.
【5】于晓飞. 304、316不锈钢晶间腐蚀的实验与理论研究[D]. 济南:山东大学, 2010:1-118.
【6】李神速. 双回路EPR法测定奥氏体不锈钢的敏化[J]. 腐蚀科学与防护技术, 2000, 12(5):288-291.
【7】塞德赖克斯 A 约翰. 不锈钢的腐蚀[M]. 北京:机械工业出版社, 1986.
【8】许淳淳. 化学工业中的腐蚀与防护[M]. 北京:化学工业出版社, 2001.
【9】柳昌义, 吴全胜, 陈慎豪, 等. 恒电位脉冲法检测奥氏体不锈钢敏化[J]. 中国腐蚀与防护学报, 1994, 14(4):291-296.
【10】Rocha H J. DEW Technische Berichte[M]. Krefeld:s.l, Krefeld Deutsche Edelstahlwerke Aktiengellschaft, 1962.
【11】Cihal, Vladimir. Intergranular corrosion of steels and alloys[C]//Amsterdam:Elsevier, 1984.
【12】You Fa Yin, Roy Faulkner G. Model predictions of grain boundary chromium depletion in Inconel 690[J]. Corrosion Science, 2007, 49:2177-2197.
【13】Sahlaoui H, Sidhom H, Philibert J. Prediction of chromium depleted-zone evolution during aging of Ni-Cr-Fe alloys[J]. Acta Materialia, 2002, 50:1383-1392.
【2】李长荣, 张维敬, 张文奇. 奥氏体不锈钢敏化动力学过程模拟[J]. 中国腐蚀与防护学报, 1989, 9(4):249-260.
【3】Sourmail T, Too C H, Bhadeshia H K D H. Sensitization and evolution of chromium depleted zones in Fe-Cr-Ni-C systems[J]. ISIJ International, 2003, 43:1814-1820.
【4】金维松, 郎宇平, 荣凡, 等. EPR法评价奥氏体不锈钢晶间腐蚀敏感性的研究[J]. 中国腐蚀与防护学报, 2007, 27(1):54-59.
【5】于晓飞. 304、316不锈钢晶间腐蚀的实验与理论研究[D]. 济南:山东大学, 2010:1-118.
【6】李神速. 双回路EPR法测定奥氏体不锈钢的敏化[J]. 腐蚀科学与防护技术, 2000, 12(5):288-291.
【7】塞德赖克斯 A 约翰. 不锈钢的腐蚀[M]. 北京:机械工业出版社, 1986.
【8】许淳淳. 化学工业中的腐蚀与防护[M]. 北京:化学工业出版社, 2001.
【9】柳昌义, 吴全胜, 陈慎豪, 等. 恒电位脉冲法检测奥氏体不锈钢敏化[J]. 中国腐蚀与防护学报, 1994, 14(4):291-296.
【10】Rocha H J. DEW Technische Berichte[M]. Krefeld:s.l, Krefeld Deutsche Edelstahlwerke Aktiengellschaft, 1962.
【11】Cihal, Vladimir. Intergranular corrosion of steels and alloys[C]//Amsterdam:Elsevier, 1984.
【12】You Fa Yin, Roy Faulkner G. Model predictions of grain boundary chromium depletion in Inconel 690[J]. Corrosion Science, 2007, 49:2177-2197.
【13】Sahlaoui H, Sidhom H, Philibert J. Prediction of chromium depleted-zone evolution during aging of Ni-Cr-Fe alloys[J]. Acta Materialia, 2002, 50:1383-1392.
相关信息