彩涂板脱漆缺陷成因与耐蚀性能
Cause of Coating Peeling and Corrosion Resistance of Colour Coated Sheets
摘 要
通过扫描电子显微镜、能谱分析、电化学阻抗及耐中性盐雾试验, 对脱漆彩涂板表面形貌、化学组成及耐蚀性能进行测试, 分析彩涂板在加工使用过程中发生局部脱漆缺陷的原因。结果表明, 脱漆缺陷导致彩涂板耐腐蚀性能明显下降, 避免脱漆缺陷应严格控制前处理钝化工艺, 保证钝化层的涂敷量和均匀性。
脱漆
耐腐蚀
钝化
colour coated sheet
coating peeling
corrosion resistance
passivation
Abstract
The surface morphology, chemical composition and corrosion resistance of the prepainted sheets with coating peeling were tested by SEM, EDS, EIS and NSST(Neutral Salt Spray Test). The cause of coating peeling and its influence on corrosion resistance of prepainted sheets were analyzed by contract testing. The improving measure was proposed to improve the machining property and corrosion resistance of the prepainted sheets.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2012/1/30
修改稿日期
网络出版日期
作者单位点击查看
备注王永明, 工程师, 硕士,
引用该论文: WANG Yong-ming,XU Cheng-ming,XIAO Yu,HOU Xuan-dong,ZHANG Yu,AI Fang-fang,ZHONG Bin. Cause of Coating Peeling and Corrosion Resistance of Colour Coated Sheets[J]. Corrosion & Protection, 2013, 34(1): 42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱立, 徐小连.彩色涂层钢板技术[M].北京:化学工业出版社, 2005.
【2】张凤珍, 张代儒, 张瑜.彩色涂层钢板质量的提高[J].涂料工业, 2006, 36(12):41-44.
【3】王成晓, 安德福.发展中的彩色涂层钢板生产[J].天津冶金, 2004.6(1):38-39.
【4】于武刚, 张启富, 黄建中.纳米TiO2涂层耐蚀性及抗紫外老化性能研究[J].材料保护, 2008, 41(2):14-16.
【5】范纯, 张家琪, 姜宝宇.彩涂板涂层附着力时效性能的研究[J].钢铁研究, 2007, 35(3):35-37.
【2】张凤珍, 张代儒, 张瑜.彩色涂层钢板质量的提高[J].涂料工业, 2006, 36(12):41-44.
【3】王成晓, 安德福.发展中的彩色涂层钢板生产[J].天津冶金, 2004.6(1):38-39.
【4】于武刚, 张启富, 黄建中.纳米TiO2涂层耐蚀性及抗紫外老化性能研究[J].材料保护, 2008, 41(2):14-16.
【5】范纯, 张家琪, 姜宝宇.彩涂板涂层附着力时效性能的研究[J].钢铁研究, 2007, 35(3):35-37.
相关信息