16Mn集输管线钢在含CO2凝析气田的腐蚀行为
Corrosion Behavior of 16Mn Gathering Pipeline Steel in CO2 Containing Condensate Gas Field
摘 要
对比研究了16Mn钢在模拟工况环境和实际工况环境中的腐蚀行为。采用失重法、扫描电镜(SEM)、电子能谱(EDS)和X射线衍射(XRD)等方法对试样腐蚀速率、腐蚀形貌、腐蚀产物成分进行了分析, 研究了温度和CO2分压对腐蚀速率的影响。结果表明, 16Mn钢主要发生严重的CO2腐蚀, 液相腐蚀速率大于气相腐蚀速率, 腐蚀速率随温度和CO2分压增加而增大。
16Mn钢
失效分析
CO2分压
CO2 corrosion
16Mn steel
failure analysis
CO2 partial pressure
Abstract
Corrosion behavior of 16Mn gathering pipeline steel was investigated in both lab-scale and field-scale by using various techniques including weight loss method, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The results showed that CO2 was the main factor contributing to corrosion of 16Mn gathering pipeline steel in Yakela condensate gas field, corrosion rate in liquid phase was higher than that in gas phase, corrosion rate increased with the increase of temperature and CO2 partial pressure.
中图分类号 TG172.3
所属栏目 失效分析
基金项目
收稿日期 2012/4/24
修改稿日期
网络出版日期
作者单位点击查看
联系人作者胡志兵(xbhuzb@sina.cn)
备注胡志兵, 工程师,
引用该论文: HU Zhi-bing. Corrosion Behavior of 16Mn Gathering Pipeline Steel in CO2 Containing Condensate Gas Field[J]. Corrosion & Protection, 2013, 34(3): 269
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨涛, 杨桦, 王凤江, 等.含CO2气井防腐工艺技术[J].天然气工业, 2007, 27(11):116-118.
【2】郭大蛟.均匀腐蚀实验方法[J].功能材料, 1982, (3):77.
【3】刘会, 朱世东, 赵国仙, 等.动态和静态下CO2分压对P110钢腐蚀行为的影响[J].腐蚀与防护, 2009, 8(5):551-554.
【4】林冠发, 白真权, 赵新伟, 等.CO2腐蚀产物形态结构与温度和压力的关系[J].石油机械, 2005, 33(2): 1-4.
【5】张清, 李全安, 文九巴, 等.CO2分压对油管钢CO2/H2S腐蚀的影响[J].钢铁研究学报, 2004, 16(4): 72-74.
【6】董会, 赵国仙, 薛艳, 等.CO2腐蚀环境中温度对5Cr钢腐蚀性能的影响[J].腐蚀与防护, 2010, 31(5):365-368.
【2】郭大蛟.均匀腐蚀实验方法[J].功能材料, 1982, (3):77.
【3】刘会, 朱世东, 赵国仙, 等.动态和静态下CO2分压对P110钢腐蚀行为的影响[J].腐蚀与防护, 2009, 8(5):551-554.
【4】林冠发, 白真权, 赵新伟, 等.CO2腐蚀产物形态结构与温度和压力的关系[J].石油机械, 2005, 33(2): 1-4.
【5】张清, 李全安, 文九巴, 等.CO2分压对油管钢CO2/H2S腐蚀的影响[J].钢铁研究学报, 2004, 16(4): 72-74.
【6】董会, 赵国仙, 薛艳, 等.CO2腐蚀环境中温度对5Cr钢腐蚀性能的影响[J].腐蚀与防护, 2010, 31(5):365-368.
相关信息