Preparation of (Ni-P)/(TiO2/ZnO) Composite Coating and its Anti-corrosion Behavior in Natural Seawater
摘 要
采用化学镀和溶胶-凝胶技术在碳钢表面制备了(Ni-P)/(TiO2/ZnO)复合涂层。采用光学显微镜、扫面电镜观察涂层表面形貌; 采用能谱及X射线衍射技术分析涂层的成分和相组成; 采用电化学极化曲线及阻抗谱评价涂层在天然海水中的耐蚀性。结果表明, (Ni-P)/(TiO2/ZnO)复合涂层较之Ni-P涂层具有更好的耐海水腐蚀性能; 在Ni-P涂层表面直接制备TiO2/ZnO复合薄膜并进行350 ℃热处理所获得的复合涂层具有最优的耐天然海水腐蚀性能。
Abstract
(Ni-P)/(TiO2/ZnO) composite coatings were prepared on carbon steel by electroless deposition technique and sol-gel method. The surface morphology and phase composition of the coating were characterized by optical microscopy, scanning electron microscopy, and X-ray diffraction. The anti-corrosion behavior in natural seawater was assessed by measurements of potentiodynamic polarization curves and electrochemical impedance spectroscopy. The results showed that the (Ni-P)/(TiO2/ZnO) composite coating had better anti-corrosion behavior than the Ni-P coating. The composite coating fabricated by preparing TiO2/ZnO thin films directly on the Ni-P coating and then processing heat treatment at 350℃ had the best anti-corrosion property in seawater.
中图分类号 TG174.3
所属栏目 试验研究
基金项目 山东省优秀中青年科学家科研奖励基金(BS2009CL016); 中央高校基本科研业务费专项资金(201113002)
收稿日期 2012/5/28
修改稿日期
网络出版日期
作者单位点击查看
备注田进涛, 副教授, 博士,
引用该论文: YU Dong-yun,XU Xing-ming,TIAN Jin-tao. Preparation of (Ni-P)/(TiO2/ZnO) Composite Coating and its Anti-corrosion Behavior in Natural Seawater[J]. Corrosion & Protection, 2013, 34(4): 298
被引情况:
【1】张 菁,刘 峥,郭亚晋,莫国芳, "Ni-P-SnO2复合镀层的制备及其性能",腐蚀与防护 37, 693-700(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘剑福, 李刚.材料腐蚀与控制工程 [M].北京: 北京大学出版社, 2010.
【2】Jin J G, Lee S K, Kim Y H. Adhesion improvement of electroless plated Ni layer by ultrasonic agitation during zincating process [J].Thin Solid Films, 2004, 466(1/2):272-278.
【3】Staia M H, Puchia E S, Castroa G, et al. Effect of thermal history on the microhardness of electroless Ni-P [J].Thin Solid Films, 1999, 355(4):472-479.
【4】Wang J F, Tian J T, Liu X Z, et al. Eeffect of polyterafluoroethylene content on electrochemical anticorrosion behaviors of electroless deposited Ni-P and Ni-P-polyterafluoroethylene coatings in seawater [J].Thin Solid Films, 2011, 519(12):5905-5911.
【5】Ohko Y, Saitoh S. Photoelectrochemical anticorrosion and self-cleaning effect of a TiO2 coating for type 304 stainless steel [J].Journal of the Electrochemical Society, 2001, 148(1):24-28.
【6】Zhang F, Chen S G, Dong L H, et al. Preparation of superhydrophobic films on titanium as effective corrosion barriers [J].Applied Surface Science, 2011, 257(12):2587-2591.
【7】Floyd F, Avudaiappan S, Gibson J, et al.Using electrochemical impedance spectroscopy to predict the corrosion resistance of unexposed coated metal panels [J].Progress in Organic Coatings, 2009, 66(1):8-34.
【8】曹楚南, 张鉴清.电化学阻抗谱导论[M].北京: 科学出版社, 2002.
【2】Jin J G, Lee S K, Kim Y H. Adhesion improvement of electroless plated Ni layer by ultrasonic agitation during zincating process [J].Thin Solid Films, 2004, 466(1/2):272-278.
【3】Staia M H, Puchia E S, Castroa G, et al. Effect of thermal history on the microhardness of electroless Ni-P [J].Thin Solid Films, 1999, 355(4):472-479.
【4】Wang J F, Tian J T, Liu X Z, et al. Eeffect of polyterafluoroethylene content on electrochemical anticorrosion behaviors of electroless deposited Ni-P and Ni-P-polyterafluoroethylene coatings in seawater [J].Thin Solid Films, 2011, 519(12):5905-5911.
【5】Ohko Y, Saitoh S. Photoelectrochemical anticorrosion and self-cleaning effect of a TiO2 coating for type 304 stainless steel [J].Journal of the Electrochemical Society, 2001, 148(1):24-28.
【6】Zhang F, Chen S G, Dong L H, et al. Preparation of superhydrophobic films on titanium as effective corrosion barriers [J].Applied Surface Science, 2011, 257(12):2587-2591.
【7】Floyd F, Avudaiappan S, Gibson J, et al.Using electrochemical impedance spectroscopy to predict the corrosion resistance of unexposed coated metal panels [J].Progress in Organic Coatings, 2009, 66(1):8-34.
【8】曹楚南, 张鉴清.电化学阻抗谱导论[M].北京: 科学出版社, 2002.
相关信息