Ni-P-Al2O3镀层的腐蚀、冲刷腐蚀和磨损行为
Corrosion, Erosion Corrosion and Wear Behaviors of Ni-P-2O3 Coating
摘 要
采用质量损失法系统研究了65Mn板材和W6Mo5Cr4V2高速钢钻头表面的Ni-P-Al2O3镀层的腐蚀、冲蚀和磨损行为。用扫描电镜(SEM)和能谱仪(EDS)进行形貌观察和成分分析。结果表明, Ni-P-Al2O3镀层的腐蚀和冲蚀性能优于316L不锈钢, 镀层的腐蚀和冲刷腐蚀速率随介质温度升高而增大, 400 ℃热处理降低镀层的腐蚀和冲刷腐蚀抗力。镀层在Na2S, HCl和H2SO4溶液中的腐蚀速率依次增大, 在Na2S和H2SO4中发生均匀腐蚀, 而在HCl溶液中则是局部腐蚀。在大气环境中, 镀层的耐磨性不如高速钢基体。
腐蚀
冲刷腐蚀
Ni-P-Al2O3 coating
corrosion
erosion corrosion
Abstract
The corrosion, erosion-corrosion and wear behaviors of Ni-P-Al2O3 coating on the surfaces of steel 65Mn and W6Mo5Cr4V2 were systematicly studied by weight loss method. The surface morphology and chemical composition were also analyzed by means of SEM and EDS respectively. The results show that the corrosion and erosion-corrosion resistances of Ni-P-Al2O3 coating more excellent than those of 316L stainless steel, and increased with the increase of medium temperature and decreased when the steel was heat treated at 400 ℃. The corrosion rates of the Ni-P-Al2O3 coating in different solution under the same test condition were in the order of Na2S < HCl < H2SO4. The main corrosion characteristic of the Ni-P-Al2O3 coating was uniform corrosion in 20%Na2S and 20%H2SO4 solutions, localized corrosion in 20%HCl solution. The were resistance of Ni-P-Al2O3 coating is poorer than that of high-speed steel in the air.
中图分类号 TG174.4
所属栏目 试验研究
基金项目 南京工程学院创新基金重大项目(CKJA201202)
收稿日期 2012/6/21
修改稿日期
网络出版日期
作者单位点击查看
备注方信贤, 副教授, 博士,
引用该论文: FANG Xin-xian,ZHEN Rui,BA Zhi-xin,BAI Yun-qiang. Corrosion, Erosion Corrosion and Wear Behaviors of Ni-P-2O3 Coating[J]. Corrosion & Protection, 2013, 34(4): 310
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张安峰, 王豫跃, 邢建东, 等.两种涂层和两种钢在液(固)两相流中冲刷与腐蚀的交互作用[J].金属学报, 2004, 40(4): 411-415.
【2】Barik R C, Wharton J A, Wood R J K, et al. Corrosion, erosion and erosion-corrosion performance of plasma electrolytic oxidation (PEO) deposited Al2O3 coatings[J].Surf Coat Technol, 2005, 199(2/3):158-167.
【3】Stack M M, Purandare Y, Hovsepian P. Impact angle effects on the erosion-corrosion of superlattice PVD coatings[J].Surf Coat Technol, 2004, 188/189(11/12): 556-565.
【4】Alirezaei S, Monirvaghefi S M, Salehi M, et al. Wear behavior of Ni-P and Ni-P-Al2O3 electroless coatings[J].Wear, 2007, 262(7/8): 978-985.
【5】Balaraju J N, Kalavati, Rajam K S. Influence of particle size on the microstructure, hardness and corrosion resistance of electroless Ni-P-Al2O3 composite coatings[J].Surf Coat Technol, 2006, 200(12/13):3933-3941.
【6】Gao J Q, Wu Y T, Liu L, et al. Crystallization behavior of nanometer-sized Al2O3 composite coatings prepared by electroless deposition[J].Mater Lett, 2005, 59(2/3):391-394.
【2】Barik R C, Wharton J A, Wood R J K, et al. Corrosion, erosion and erosion-corrosion performance of plasma electrolytic oxidation (PEO) deposited Al2O3 coatings[J].Surf Coat Technol, 2005, 199(2/3):158-167.
【3】Stack M M, Purandare Y, Hovsepian P. Impact angle effects on the erosion-corrosion of superlattice PVD coatings[J].Surf Coat Technol, 2004, 188/189(11/12): 556-565.
【4】Alirezaei S, Monirvaghefi S M, Salehi M, et al. Wear behavior of Ni-P and Ni-P-Al2O3 electroless coatings[J].Wear, 2007, 262(7/8): 978-985.
【5】Balaraju J N, Kalavati, Rajam K S. Influence of particle size on the microstructure, hardness and corrosion resistance of electroless Ni-P-Al2O3 composite coatings[J].Surf Coat Technol, 2006, 200(12/13):3933-3941.
【6】Gao J Q, Wu Y T, Liu L, et al. Crystallization behavior of nanometer-sized Al2O3 composite coatings prepared by electroless deposition[J].Mater Lett, 2005, 59(2/3):391-394.
相关信息