Effect of Imidazoline Inhibitors on Corrosion Performance of J55 Steel in Simulated CO2 Flooding Environment
摘 要
采用极化曲线和电化学阻抗谱方法研究了模拟CO2驱环境中两种咪唑啉类缓蚀剂对J55钢的缓蚀性能。利用拟合得到了电化学腐蚀的热动力学参数并对其进行了分析, 同时计算了两种缓蚀剂对J55钢的缓蚀效率。结果表明, 腐蚀电流密度(Jcorr)均随缓蚀剂用量提高而不断减小, 缓蚀剂作用下的电荷传递电阻Rt均远远大于空白试验条件下的Rt值, 改性咪唑啉缓蚀剂比咪唑啉缓蚀剂对CO2腐蚀具有更好的缓蚀效果。
Abstract
The effect of inhibitors on the performance of J55 steel in simulated CO2 flooding environment added two kinds of imidazoline inhibitors was investigated by means of polarization curves and electrochemical impedance spectroscopy(EIS). The parameters of thermal dynamics of electrochemical corrosion were fitted and analyzed, and the inhibition efficiencies were also calculated. The results indicated that the corrosion current density decreased with increasing the contents of inhibitors. Due to the effect of inhibitors, the charge transfer resistance was greater than that under the blank condition. In addition, modified imidazoline inhibitor has better inhibition performance than imidazoline inhibitor for CO2 corrosion.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 陕西延长石油(集团)有限责任公司研究院青年基金(YJY2012-QNJJ-07)
收稿日期 2013/1/11
修改稿日期
网络出版日期
作者单位点击查看
备注尹志福,博士,
引用该论文: YIN Zhi-fu,LI Hui,LIU Li,MA Bin,WANG Ke. Effect of Imidazoline Inhibitors on Corrosion Performance of J55 Steel in Simulated CO2 Flooding Environment[J]. Corrosion & Protection, 2013, 34(6): 489
被引情况:
【1】张永刚,罗懿,刘学全,熊佩,魏开鹏,斯容, "红河油田CO2/泡沫驱缓蚀剂研究与应用",腐蚀与防护 35, 899-902(2014)
【2】王珂,张永强,尹志福,吕雷,朱世东, "N80和3Cr油管钢在CO2驱油环境中的腐蚀行为",腐蚀与防护 36, 706-710(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马涛,汤达祯,蒋平,等. 注CO2提高采收率技术现状[J]. 油田化学,2007,24(4):379-383.
【2】祝春生,程林松. 低渗透油藏CO2驱提高原油采收率评价研究[J]. 钻采工艺,2007,30(6):55-60.
【3】苏俊华,张学元,王凤平,等. 饱和CO2的高矿化度溶液中咪唑啉缓蚀机理的研究[J]. 材料保护,1999,32(5):32-33.
【4】蒋秀,骆素珍,郑玉贵,等. 炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3% NaCl溶液的缓蚀性能研究[J]. 中国腐蚀与防护学报,2004,24(1):10-15.
【5】Liu F G,Du M. Electrochemical behavior of Q235 steel in saltwater saturated with carbon dioxide based on new imidazoline derivative inhibitor[J]. Corrosion Science,2009,51(1):102-109.
【6】Ramachandran S,Ahn Y S,Greaves M,et al. Development of high temperature,high pressure corrosion Inhibitor[C]//Corrosion 2006. Houston:[s.n.],2006:6377.
【7】Juttner K. Electrochemical impedance spectroscopy (EIS) of corrosion process on inhomogeneous surfaces[J]. Electrochimica Acta,1990,35(10):1501-1508.
【8】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2004.
【2】祝春生,程林松. 低渗透油藏CO2驱提高原油采收率评价研究[J]. 钻采工艺,2007,30(6):55-60.
【3】苏俊华,张学元,王凤平,等. 饱和CO2的高矿化度溶液中咪唑啉缓蚀机理的研究[J]. 材料保护,1999,32(5):32-33.
【4】蒋秀,骆素珍,郑玉贵,等. 炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3% NaCl溶液的缓蚀性能研究[J]. 中国腐蚀与防护学报,2004,24(1):10-15.
【5】Liu F G,Du M. Electrochemical behavior of Q235 steel in saltwater saturated with carbon dioxide based on new imidazoline derivative inhibitor[J]. Corrosion Science,2009,51(1):102-109.
【6】Ramachandran S,Ahn Y S,Greaves M,et al. Development of high temperature,high pressure corrosion Inhibitor[C]//Corrosion 2006. Houston:[s.n.],2006:6377.
【7】Juttner K. Electrochemical impedance spectroscopy (EIS) of corrosion process on inhomogeneous surfaces[J]. Electrochimica Acta,1990,35(10):1501-1508.
【8】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2004.
相关信息