Inhibition Behavior of 4-Aminoantipyrine on Carbon Steel in HCl Solution
摘 要
采用失重法、动电位极化曲线、电化学阻抗谱研究了4-氨基安替比林在盐酸介质中对碳钢的缓蚀行为。结果表明, 4-氨基安替比林是一种同时抑制阳极和阴极反应的混合型缓蚀剂, 缓蚀效率随缓蚀剂浓度增加而增大, 4-氨基安替比林在碳钢表面的吸附吉布斯自由能为-30.52 kJ·mol-1, 是一种介于物理吸附与化学吸附之间的混合型自发吸附, 符合Langmuir等温吸附式。
Abstract
The inhibition behavior of 4-Aminoantipyrine on carbon steel in HCl solution was studied by weight loss testing, potentiodynamic polarization curvers and electrochemical impedance spectroscopy. The results show that the inhibition efficiency increased with the increase of 4-Aminoantipyrine concentration. 4-Aminoantipyrine is a mix-type inhibitor which can inhibit the reaction of anode and cathode, and the standard free Gibbs energy of adsorption is -30.52 kJ·mol-1, which indicates that 4-Aminoantipyrine can adhere on carbon steel surface with a kind of spontaneous adsorption model between physical adsorption and chemical adsorption, and obeys Langmuir isotherm.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 材料腐蚀与防护四川省重点实验室开放基金(2011CL13); 四川理工学院大学生创新基金(cx20121303)
收稿日期 2013/1/4
修改稿日期
网络出版日期
作者单位点击查看
备注蔡述兰,副教授,学士,
引用该论文: CAI Shu-lan,QIAO Kang-quan,REN De-hu,HE Lei-jin,ZHANG Xiao-lan. Inhibition Behavior of 4-Aminoantipyrine on Carbon Steel in HCl Solution[J]. Corrosion & Protection, 2013, 34(7): 576
被引情况:
【1】余强,陈阵,魏昶, "硫脲对HR-2不锈钢的缓蚀性",腐蚀与防护 35, 116-119(2014)
【2】向云刚,谯康全,崔益顺, "茄叶提取液在盐酸介质中对碳钢的缓蚀性能",腐蚀与防护 37, 122-127(2016)
【3】向云刚,崔益顺,谯康全, "十二烷基二羟乙基氧化胺在0.5 mol·L-1 H2SO4中对A3钢的缓蚀性能",腐蚀与防护 37, 30-34(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Hasanova R,Bilgeb S,Bilgi S,et al. Experimental and theoretical calculations on corrosion inhibition of steel in 1 M H2SO4 by crown type polyethers[J]. Corrosion Science,2010,52(5):984-990.
【2】Raja P B,Sethuraman M G. Natural products as corrosion inhibitor for metals in corrosive media-a review[J]. Materials Letters,2008,15(1):113-116.
【3】杨尚军,谭世语,张研. 生物缓蚀剂的研究进展[J]. 表面技术,2006,35(1):12-13,73.
【4】Praveen B M,Venkatesha T V. Metol as corrosion inhibitor for steel[J]. International Journal of Electrochemical Science,2009,4(1):267-275.
【5】Khaled K F. New synthesized guanidine derivative as a green corrosio inhibitor for mild steel in acidic solutions[J]. International Journal of Electrochemical Science,2008,30(3):462-475.
【6】闫莹,李伟华,邢少华,等. 新型杂环化合物在1 M HCl中对Q235钢的缓蚀性能研究[J]. 腐蚀科学与防护技术,2007,12(6):414-418.
【7】王招娣,司云森,余强,等. 一种曼尼希碱在酸性介质中对碳钢缓蚀行为的研究[J]. 表面技术,2011,40(1):59-62,80.
【8】曹楚南. 腐蚀电化学原理(第三版)[M]. 北京:化学工业出版社,2008.
【9】陈文. 碳钢缓蚀剂和铜基自组装膜的研究[D]. 重庆:西南大学硕士学位论,2012.
【10】赵丽娜,许淳淳. 无机复合缓蚀剂对碳钢的缓蚀性能[J]. 腐蚀与防护,2008,29(8):460-463.
【11】Kissi M,Bourklah M,Hammouti B,et al. Establishment of equivalent circuits from electrochemical impedance spectroscopy study of corrosion inhibition of steel by pyrazine in sulphuric acidic solution[J]. Applied Surface Science,2006,52(12):4190-4197.
【12】宋伟伟,张静,杜敏. 新型不对称双季铵盐缓蚀剂在HCl中对Q235钢的缓蚀行为[J]. 化学学报,2010,69(16):1851-1857.
【2】Raja P B,Sethuraman M G. Natural products as corrosion inhibitor for metals in corrosive media-a review[J]. Materials Letters,2008,15(1):113-116.
【3】杨尚军,谭世语,张研. 生物缓蚀剂的研究进展[J]. 表面技术,2006,35(1):12-13,73.
【4】Praveen B M,Venkatesha T V. Metol as corrosion inhibitor for steel[J]. International Journal of Electrochemical Science,2009,4(1):267-275.
【5】Khaled K F. New synthesized guanidine derivative as a green corrosio inhibitor for mild steel in acidic solutions[J]. International Journal of Electrochemical Science,2008,30(3):462-475.
【6】闫莹,李伟华,邢少华,等. 新型杂环化合物在1 M HCl中对Q235钢的缓蚀性能研究[J]. 腐蚀科学与防护技术,2007,12(6):414-418.
【7】王招娣,司云森,余强,等. 一种曼尼希碱在酸性介质中对碳钢缓蚀行为的研究[J]. 表面技术,2011,40(1):59-62,80.
【8】曹楚南. 腐蚀电化学原理(第三版)[M]. 北京:化学工业出版社,2008.
【9】陈文. 碳钢缓蚀剂和铜基自组装膜的研究[D]. 重庆:西南大学硕士学位论,2012.
【10】赵丽娜,许淳淳. 无机复合缓蚀剂对碳钢的缓蚀性能[J]. 腐蚀与防护,2008,29(8):460-463.
【11】Kissi M,Bourklah M,Hammouti B,et al. Establishment of equivalent circuits from electrochemical impedance spectroscopy study of corrosion inhibition of steel by pyrazine in sulphuric acidic solution[J]. Applied Surface Science,2006,52(12):4190-4197.
【12】宋伟伟,张静,杜敏. 新型不对称双季铵盐缓蚀剂在HCl中对Q235钢的缓蚀行为[J]. 化学学报,2010,69(16):1851-1857.
相关信息