CO2/O2 Corrosion Behavior of TP100 Steel in High Temperature and High Pressure Environment
摘 要
采用失重法、X射线衍射方法(XRD)、扫描电镜观察及其能谱分析等方法研究了TP100钢在含O2,CO2以及CO2与O2共存3种环境中的腐蚀行为。结果表明,在有CO2与O2共存环境中,TP100钢的腐蚀速率显著高于CO2或O2两种气体单独存在条件下。在有CO2与O2共存环境中,TP100钢表面形成主要由FeCO3,Fe3O4和Fe2O3组成的疏松多孔的腐蚀产物,这种多孔的腐蚀产物为腐蚀气体和溶液提供了快速通道从而促进了腐蚀,在基体表面出现了明显的蚀坑。
Abstract
The corrosion behavior of TP100 steel in CO2 and O2 coexisting condition was studied using weight loss method, scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and X-ray diffraction (XRD). The results show that the CO2-O2 corrosion rate of TP100 steel is remarkably higher than that of CO2 corrosion or O2 corrosion, respectively. CO2-O2 corrosion scale is loose, composed of FeCO3, Fe2O3 and Fe3O4, and lots of pores exist in the corrosion scale. The porous scale provided fast transferring channel for corrosive solution, and as a result, obvious pits appeared on the surface.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2013/5/16
修改稿日期
网络出版日期
作者单位点击查看
备注柳伟,副教授,博士,
引用该论文: LIN Xue-qiang,LIU Wei,ZHANG Jing,DONG Shuai,ZHANG Hai-long,LI Xiao-bo,CAI Feng,XU Chuan-chuan,LU Min-xu. CO2/O2 Corrosion Behavior of TP100 Steel in High Temperature and High Pressure Environment[J]. Corrosion & Protection, 2013, 34(8): 698
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙建波,柳伟,常炜,等. 低铬X65管线钢CO2腐蚀产物膜的特征及形成机制[J]. 金属学报,2009,45(1):84-90.
【2】Van Hunnik E W J,Pots B F M,Hendriksen E L J A. The formation of protective FeCO3 corrosion product layers in CO2 corrosion[C]//The 51st NACE Annual Conference,Houston: [s.n.],1996:96006.
【3】Gao M,Pang X,Gao K. The growth mechanism of CO2 corrosion product films[J]. Corrosion Science,2011,53(2):557-568.
【4】Kermani M B,Morshed A. Carbon dioxide corrosion in oil and gasproduction-a compendium[J]. Corrosion,2003:59(3):659-669.
【5】路民旭,白真权,赵新伟,等. 油气采集储运中的腐蚀现状及典型案例[J]. 腐蚀与防护,2002,23(2):105-107.
【6】郭少强,许立宁,常炜,等. 3Cr管线钢CO2腐蚀实验研究[J]. 金属学报,2011,8(47):1067-1074.
【7】Drela I,Falewicz P,Kuczkowska S. New rapid test for evaluation of scale inhibitors[J]. Water Research,1998,32(2):3188-3191.
【2】Van Hunnik E W J,Pots B F M,Hendriksen E L J A. The formation of protective FeCO3 corrosion product layers in CO2 corrosion[C]//The 51st NACE Annual Conference,Houston: [s.n.],1996:96006.
【3】Gao M,Pang X,Gao K. The growth mechanism of CO2 corrosion product films[J]. Corrosion Science,2011,53(2):557-568.
【4】Kermani M B,Morshed A. Carbon dioxide corrosion in oil and gasproduction-a compendium[J]. Corrosion,2003:59(3):659-669.
【5】路民旭,白真权,赵新伟,等. 油气采集储运中的腐蚀现状及典型案例[J]. 腐蚀与防护,2002,23(2):105-107.
【6】郭少强,许立宁,常炜,等. 3Cr管线钢CO2腐蚀实验研究[J]. 金属学报,2011,8(47):1067-1074.
【7】Drela I,Falewicz P,Kuczkowska S. New rapid test for evaluation of scale inhibitors[J]. Water Research,1998,32(2):3188-3191.
相关信息