CO2/H2S分压比对BG90SS材质腐蚀行为的影响
Influence of CO2/H2S Partial Pressure Ratio on Corrosion Behavior of BG90SS Material
摘 要
采用高温高压反应釜模拟阿姆河气田腐蚀环境,研究了不同CO2/H2S分压比对BG90SS钢腐蚀行为的影响。结果表明,随着CO2/H2S分压比的减小,BG90SS钢的腐蚀速率减小。通过对腐蚀产物膜的分析,发现腐蚀产物主要是马基诺矿(四方硫铁矿),说明在此条件下BG90SS钢的腐蚀行为主要受H2S控制。
BG90SS
腐蚀速率
腐蚀产物
CO2/H2S partial pressure ratio
BG90SS
corrosion rate
corrosion product
Abstract
The influence of CO2/H2S partial pressure ratio on the corrosion behavior of BG90SS was studied bysimulating the corrosion environment of Amu Daryagas field with a high pressure and high temperature autoclave.The results show that with the decrease of CO2/H2S partial pressure ratio,the material corrosion rate decreased.From the analysis of corrosion product film,mackinawite was the major corrosion product.This indicates that in thiscorrosive environment the corrosion behavior of BG90SS material is controlled by H2S.
中图分类号 TG172.3
所属栏目 试验研究
基金项目 国家科技重大专项(2011ZX05059)
收稿日期 2013/1/14
修改稿日期
网络出版日期
作者单位点击查看
备注裘智超,助理工程师,硕士,
引用该论文: QIU Zhi-chao,LIU Xiang,ZHAO Zhi-hong,YE Zheng-rong,ZHAO Chun,WANG Chun-cai. Influence of CO2/H2S Partial Pressure Ratio on Corrosion Behavior of BG90SS Material[J]. Corrosion & Protection, 2013, 34(11): 981
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】阎伟,邓金根,董星亮,等.油管钢在CO2/H2S环境中的腐蚀产物及腐蚀行为[J]. 腐蚀与防护,2011,32(3):193-196.
【2】王召民,兰旭,赵景茂.L360钢在高压H2S/CO2环境气液两相中的腐蚀行为[J]. 腐蚀与防护,2011,32(10):782-784.
【3】Srinivasan S,Kane R D.Experimental simulation ofmultiphase CO2/H2S system[J].Corrosion,1999(14):1168-1182.
【4】卢绮敏.石油工业中的腐蚀与防护[M].北京:化学工业出版社, 2001.
【2】王召民,兰旭,赵景茂.L360钢在高压H2S/CO2环境气液两相中的腐蚀行为[J]. 腐蚀与防护,2011,32(10):782-784.
【3】Srinivasan S,Kane R D.Experimental simulation ofmultiphase CO2/H2S system[J].Corrosion,1999(14):1168-1182.
【4】卢绮敏.石油工业中的腐蚀与防护[M].北京:化学工业出版社, 2001.
相关信息