烧结温度对316不锈钢粉末冶金烧结体组织和性能的影响
Influence of Sintering Temperature on Microstructure and Properties of 316 Stainless Steel Powder Metallurgy Sintered Body
摘 要
采用真空烧结法制备了316奥氏体不锈钢粉末冶金烧结体, 研究了烧结温度对其显微组织和力学性能的影响, 并对其拉伸断口形貌进行了分析。结果表明: 随着烧结温度的提高, 烧结体组织晶粒不断粗化, 孔隙减少、尺寸降低; 烧结体的相对密度、抗拉强度、屈服强度、伸长率等均提高, 但当温度升到1 340 ℃以后提高并不明显, 并有缓慢降低的趋势; 最佳烧结温度为1 340 ℃, 此时烧结体的密度为7.86 g·cm-3, 抗拉强度为754 MPa。
烧结温度
不锈钢
力学性能
powder metallurgy
sintering temperature
stainless steel
mechanical property
Abstract
316 austenitic stainless steel powder metallurgy sintered body was fabricated by vacuum sintering method, and the influence of sintering temperature on the microstructure and mechanical properties was studied. The tensile fracture surface morphology was analyzed. The results show that the grains coarsened gradually, pores reduced and size decreased, the relative density, tensile strength, yield strength and elongation of the sintered body increased obviously with the increase of sintering temperature, while increased unobviously when the temperature reached 1 340 ℃ and even decreased slowly. The optimal sintering temperature was 1 340 ℃, the density and tensile strength of the sintered bady could reach 7.86 g·cm-3 and 754 MPa, respectively.
中图分类号 TF124.5
所属栏目
基金项目 国家“863”计划资助项目(2007AA03Z115); 湖北省重点学科“机械电子工程”资助项目
收稿日期 2009/12/17
修改稿日期 2010/8/2
网络出版日期
作者单位点击查看
备注蔺绍江(1979-), 男, 湖南浏阳人, 博士研究生。
引用该论文: LIN Shao-jiang,XIONG Wei-hao,YAO Zhen-hua,QU Jun. Influence of Sintering Temperature on Microstructure and Properties of 316 Stainless Steel Powder Metallurgy Sintered Body[J]. Materials for mechancial engineering, 2011, 35(1): 22～25
蔺绍江,熊惟皓,姚振华,瞿峻. 烧结温度对316不锈钢粉末冶金烧结体组织和性能的影响[J]. 机械工程材料, 2011, 35(1): 22～25
被引情况:
【1】余小鲁,汪太平, "造孔剂含量对粉末冶金不锈钢多孔材料孔隙率和抗压强度的影响",机械工程材料 36, 60-62(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张胜寒, 李娜, 杨妮.316不锈钢的晶间腐蚀行为的研究[J].汽轮机技术, 2009(1): 78-80.
【2】柴田·俊夫.不锈钢腐蚀研究的展望(一)[J].设备管理与维修, 1997(7): 43-45.
【3】果世驹, 杨霞, 陈邦峰, 等.粉末316L不锈钢的高密度强化烧结机[J].机械工程材料, 2004, 28(7): 7-11.
【4】WANG Le, YI Jian-hong, DAI Yu, et al. Influence of compacting pressure on properties of sinter-hardening P/M steels[J].Materials Science and Engineering of Powder Metallurgy, 2008, 13(2): 97-101.
【5】WHITTAKER D. Process economics and technological advances in P/M automotive parts[J].Int J Powder Metal, 1998, 34(3): 17-24.
【6】何朋, 王均安, 徐新平.粉末冶金制备不锈钢的研究及发展[J].金属热处理, 2004(7): 1-5.
【7】吴恩熙, 吴爱华.烧结温度对高钨重合金性能的影响[J].稀有金属与硬质合金, 2004, 32(1): 16-18.
【8】王丹丹, 李溪滨, 刘如铁, 等.烧结温度对Ni-Cr-Mo合金性能的影响[J].材料科学与工程学报, 2004, 22(6): 896-900.
【9】王栋梁, 徐自伟, 况春江, 等.烧结温度对注射成形Cr-Mn-Mo-N不锈钢零件组织与性能的影响[J].粉末冶金工业, 2009, 19(1): 11-15.
【10】杨发展, 赵军, 艾兴, 等.烧结温度对WZV材料力学性能和显微结构的影响[J].材料科学与工艺, 2009(3): 364-372.
【11】王乐, 易健宏, 戴煜, 等.压制压力对粉末冶金烧结硬化钢性能的影响[J].粉末冶金材料科学与工程, 2008(2): 97-101.
【12】XU X, LIU Y, GERMAN R M. Reconciliation of sintering theory with sintering practice[J].Metal Powder Report, 2001, 56(9): 37-39.
【2】柴田·俊夫.不锈钢腐蚀研究的展望(一)[J].设备管理与维修, 1997(7): 43-45.
【3】果世驹, 杨霞, 陈邦峰, 等.粉末316L不锈钢的高密度强化烧结机[J].机械工程材料, 2004, 28(7): 7-11.
【4】WANG Le, YI Jian-hong, DAI Yu, et al. Influence of compacting pressure on properties of sinter-hardening P/M steels[J].Materials Science and Engineering of Powder Metallurgy, 2008, 13(2): 97-101.
【5】WHITTAKER D. Process economics and technological advances in P/M automotive parts[J].Int J Powder Metal, 1998, 34(3): 17-24.
【6】何朋, 王均安, 徐新平.粉末冶金制备不锈钢的研究及发展[J].金属热处理, 2004(7): 1-5.
【7】吴恩熙, 吴爱华.烧结温度对高钨重合金性能的影响[J].稀有金属与硬质合金, 2004, 32(1): 16-18.
【8】王丹丹, 李溪滨, 刘如铁, 等.烧结温度对Ni-Cr-Mo合金性能的影响[J].材料科学与工程学报, 2004, 22(6): 896-900.
【9】王栋梁, 徐自伟, 况春江, 等.烧结温度对注射成形Cr-Mn-Mo-N不锈钢零件组织与性能的影响[J].粉末冶金工业, 2009, 19(1): 11-15.
【10】杨发展, 赵军, 艾兴, 等.烧结温度对WZV材料力学性能和显微结构的影响[J].材料科学与工艺, 2009(3): 364-372.
【11】王乐, 易健宏, 戴煜, 等.压制压力对粉末冶金烧结硬化钢性能的影响[J].粉末冶金材料科学与工程, 2008(2): 97-101.
【12】XU X, LIU Y, GERMAN R M. Reconciliation of sintering theory with sintering practice[J].Metal Powder Report, 2001, 56(9): 37-39.
相关信息