焊剂中加入CeO2对E36钢埋弧焊焊缝组织与性能的影响
Effect of Adding CeO2 to Flux on Microstructure and Properties of SAW Seam of E36 Steel
摘 要
通过向研制的高碱度焊剂中加入质量分数为0%, 2%, 4%的稀土氧化铈(CeO2), 实现向焊缝金属中添加不同含量的稀土, 研究了不同含量的CeO2对焊缝金属显微组织和性能的影响。结果表明:加入稀土后的焊缝组织以针状铁素体为主, 晶粒得到了细化, 焊缝的冲击韧性明显改善;其中, 焊剂中CeO2加入量为2%的焊缝金属的冲击性能要好于加入量为4%的。
焊缝金属
冲击韧性
针状铁素体
rear earth CeO2
welding seam metal
impact toughness
acicular ferrite
Abstract
Through adding rare earth(RE) ceria (CeO2, 0wt%, 2wt% and 4wt%) to the developed high basicity flux, the different contents of RE elements were added to the welding seam metal. The effects of different contents of CeO2 on microstructure and properties of the welding seam metal were investigated. The results show that microstructure of the welding seam with RE was main acicular ferrite, the grains were refined and impact toughness of the seam was improved significantly. The impact properties of the welding seam metal with flux containing 2wt% CeO2 were better than those with 4wt% CeO2.
中图分类号 TG423 TG445
所属栏目
基金项目 教育部博士点基金资助项目(200804870034)
收稿日期 2010/1/25
修改稿日期 2010/12/3
网络出版日期
作者单位点击查看
备注徐慧子(1983-), 女, 山东威海人, 硕士研究生。
引用该论文: XU Hui-zi,YU Sheng-fu,HUANG Lin-bing,LI Guo-fei,YU Lu. Effect of Adding CeO2 to Flux on Microstructure and Properties of SAW Seam of E36 Steel[J]. Materials for mechancial engineering, 2011, 35(2): 24～26
徐慧子,余圣甫,黄林兵,李国飞,余璐. 焊剂中加入CeO2对E36钢埋弧焊焊缝组织与性能的影响[J]. 机械工程材料, 2011, 35(2): 24～26
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】ZHANG Z Y, FARRAR R A. Columnar gtrain development in C-Mn-Ni low alloy weld metals and the influence of nickel[J].Journal of Materials Science, 1995, 30 (22):5581-5588.
【2】ZHU Y Z, FARRAR R A. Influence of Mn and Ni of microstructure and toughness of C-Mn-Ni welds metals[J].Welding Journal, 1997, 76(5):183-196.
【3】韩顺昌.针状铁素体的物理冶金学(续) [J].材料开发与应用, 1995, 10(6):2-8.
【4】薛海涛, 李建国, 李俊岳.焊条药皮中稀土氧化物向焊缝中过渡机制的研究[J].中国稀土学报, 2003(5):580-583.
【5】郭永环, 范西营, 王广丰.氧化铈对低合金钢焊条力学性能的影响[J].焊接学报, 2009(2): 41-44.
【6】邱巨峰, 余宗森.稀土在晶界存在形式及对晶界状态的影响[J].稀土, 1983, 32(4):58-68.
【7】陈岁元, 江自应.稀土在钢铁中的作用与机理研究[J].云南冶金, 1998, 27(3):1-4.
【8】余景生, 余宗森, 章复中.稀土处理钢手册[M].北京:冶金工业出敝社, 1993.
【9】王世亮, 胡维平, 唐伯钢.采用重稀土改善焊缝韧性的研究[J].焊接学报, 1986(2):55-62.
【10】杨军, 范红刚, 薛锦.低合金高强钢焊缝针状铁素体形核问题的探讨[J].西安交通大学学报, 1998(9):89-93.
【11】杨军, 吴鲁海, 茅及放.低合金高强钢焊缝熔敷金属强韧化机理[J].焊接学报, 2006(3):86-90.
【2】ZHU Y Z, FARRAR R A. Influence of Mn and Ni of microstructure and toughness of C-Mn-Ni welds metals[J].Welding Journal, 1997, 76(5):183-196.
【3】韩顺昌.针状铁素体的物理冶金学(续) [J].材料开发与应用, 1995, 10(6):2-8.
【4】薛海涛, 李建国, 李俊岳.焊条药皮中稀土氧化物向焊缝中过渡机制的研究[J].中国稀土学报, 2003(5):580-583.
【5】郭永环, 范西营, 王广丰.氧化铈对低合金钢焊条力学性能的影响[J].焊接学报, 2009(2): 41-44.
【6】邱巨峰, 余宗森.稀土在晶界存在形式及对晶界状态的影响[J].稀土, 1983, 32(4):58-68.
【7】陈岁元, 江自应.稀土在钢铁中的作用与机理研究[J].云南冶金, 1998, 27(3):1-4.
【8】余景生, 余宗森, 章复中.稀土处理钢手册[M].北京:冶金工业出敝社, 1993.
【9】王世亮, 胡维平, 唐伯钢.采用重稀土改善焊缝韧性的研究[J].焊接学报, 1986(2):55-62.
【10】杨军, 范红刚, 薛锦.低合金高强钢焊缝针状铁素体形核问题的探讨[J].西安交通大学学报, 1998(9):89-93.
【11】杨军, 吴鲁海, 茅及放.低合金高强钢焊缝熔敷金属强韧化机理[J].焊接学报, 2006(3):86-90.
相关信息