制氢换热器304不锈钢盘管开裂原因分析
Cracking Analysis of 304 Stainless Steel Hydrogen Production Heat Exchanger Coil
摘 要
为了查明制氢换热器304不锈钢盘管开裂的原因, 对其宏微观组织、化学成分、断口形貌、腐蚀产物化学成分进行了分析。结果表明: 该304不锈钢盘管的开裂属于应力腐蚀开裂, 盘管的工作应力和壳程水蒸气中的微量溶解氧共同导致了盘管的开裂; 建议采用Incoloy 800铁镍基耐蚀合金替代304不锈钢制作制氢换热器盘管。
盘管
应力腐蚀开裂
换热器
304 stainless steel
coil
stress corrosion cracking
heat exchanger
Abstract
The reason of cracking of 304 stainless steel hydrogen production heat exchanger coil was found out through analysis of macrostructure, microstructure, chemical composition, morphology of fracture and chemical composition of corrosion products. The results show that, it was stress corrosion cracking of 304 stainless steel coil. Working stress of the coil and dissolved oxygen in the shell side steam led to the cracking of coil. It was suggested that adopting Incoloy 800 Fe-Ni corrosion resistant alloy to replace 304 stainless steel as material of hydrogen production heat exchanger coil.
中图分类号 TG142.71
所属栏目
基金项目
收稿日期 2010/2/10
修改稿日期 2011/1/10
网络出版日期
作者单位点击查看
备注师红旗(1982-), 男, 山西长治人, 硕士研究生。
引用该论文: SHI Hong-qi,CHEN Xu,DING Yi,MA Li-qun. Cracking Analysis of 304 Stainless Steel Hydrogen Production Heat Exchanger Coil[J]. Materials for mechancial engineering, 2011, 35(4): 98～100
师红旗,陈旭,丁毅,马立群. 制氢换热器304不锈钢盘管开裂原因分析[J]. 机械工程材料, 2011, 35(4): 98～100
被引情况:
【1】马新朝,刘璐,洪源平,李世伟,步伟东, "夹杂物对压水堆核电站用Z2CN19-10不锈钢应力腐蚀开裂的影响",机械工程材料 40, 10-14(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】钟群鹏, 赵子华.断口学[M].北京: 高等教育出版社,2006.
【2】廖景娱.金属构件失效分析[M]. 北京: 化学工业出版社,2003.
【3】黄建中, 左禹.材料的耐蚀性和腐蚀数据[M].北京: 化学工业出版社, 2003.
【2】廖景娱.金属构件失效分析[M]. 北京: 化学工业出版社,2003.
【3】黄建中, 左禹.材料的耐蚀性和腐蚀数据[M].北京: 化学工业出版社, 2003.
相关信息