Microstructure and Performance of Iron Brass Coating Produced by High Velocity Air-Fuel Spray on Steel Surface
摘 要
采用空气助燃超音速火焰喷涂技术在30CrMnSi钢基体表面上制备出厚3 mm的HFe59-1-1铁黄铜涂层, 对涂层的化学成分、物相组成、显微硬度及耐磨性能进行了研究。结果表明: 制备的铁黄铜涂层呈层状结构, 晶粒细小, 致密度高, 孔隙率小于1%, 和基体结合强度高, 显微硬度为241 HV, 且表现出比同牌号铸造铁黄铜更为优良的耐磨性能。
Abstract
Iron brass coating with thickness of 3 mm was prepared on the surface of 30CrMnSi steel substrate by high velocity air-fuel spray. The chemical composition, phase composition, micro-hardness and wear properties of the coating were investigated. The results show that the iron brass coating had layered structure, fine grains, high density, lower porosity of less than 1%, high bonding strength with the substrate and micro-hardness of 241 HV. It had better wear resistance than the as-cast iron brass with same grade.
中图分类号 TG146.1
所属栏目
基金项目
收稿日期 2010/4/19
修改稿日期 2010/12/23
网络出版日期
作者单位点击查看
备注邓畅光(1970-), 男, 广东罗定人, 高级工程师, 硕士。
引用该论文: DENG Chang-guang,DENG Chun-ming,KUANG Min,LIU Min. Microstructure and Performance of Iron Brass Coating Produced by High Velocity Air-Fuel Spray on Steel Surface[J]. Materials for mechancial engineering, 2011, 35(5): 7~10
邓畅光,邓春明,况敏,刘敏. 钢基体表面空气助燃超音速火焰喷涂制备铁黄铜涂层的组织和性能[J]. 机械工程材料, 2011, 35(5): 7~10
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李长久.超音速火焰喷涂及涂层性能简介[J].表面工程, 1996(4): 29-33.
【2】江礼, 王汉功, 侯根良, 等.低温超音速火焰喷涂铜涂层性能研究[J].兵器材料科学与工程, 2005, 28(2): 48-51.
【3】周克崧.热喷涂技术替代电镀硬铬的研究进展[J].中国有色金属学报, 2004, 14(1): 182-191.
【4】LEGOUX J G, ARSONAULT B, MOREAU C, et al. Evaluation of four high velocity thermal spray gun using WC-10Co-4Cr cermates[C]//Proceedings of the 16th International Thermal Spray Conference. Montreal: ASM International, 2000:479-486.
【5】BERGET J, ROGNE T. A summary of recent developments of HVOF sprayed ceramic-metallic coatings for corrosion and wear resistance[C]//Thermal Spray. Ohio: ASM International Materials Park, 2001:1157-1163.
【6】申永良, 李维芬.纯铜及其铜合金[J].冶金丛刊, 1998(6): 21-23.
【7】王晓峰, 刘德义, 刘世程, 等.钢/黄铜双金属管扩散复合的研究[J].有色金属加工, 2005, 34(1): 27-30.
【8】张田仓, 郭德伦.固相连接新技术——搅拌摩擦焊接技术[J].航空工艺技术, 1999(2): 35-37.
【2】江礼, 王汉功, 侯根良, 等.低温超音速火焰喷涂铜涂层性能研究[J].兵器材料科学与工程, 2005, 28(2): 48-51.
【3】周克崧.热喷涂技术替代电镀硬铬的研究进展[J].中国有色金属学报, 2004, 14(1): 182-191.
【4】LEGOUX J G, ARSONAULT B, MOREAU C, et al. Evaluation of four high velocity thermal spray gun using WC-10Co-4Cr cermates[C]//Proceedings of the 16th International Thermal Spray Conference. Montreal: ASM International, 2000:479-486.
【5】BERGET J, ROGNE T. A summary of recent developments of HVOF sprayed ceramic-metallic coatings for corrosion and wear resistance[C]//Thermal Spray. Ohio: ASM International Materials Park, 2001:1157-1163.
【6】申永良, 李维芬.纯铜及其铜合金[J].冶金丛刊, 1998(6): 21-23.
【7】王晓峰, 刘德义, 刘世程, 等.钢/黄铜双金属管扩散复合的研究[J].有色金属加工, 2005, 34(1): 27-30.
【8】张田仓, 郭德伦.固相连接新技术——搅拌摩擦焊接技术[J].航空工艺技术, 1999(2): 35-37.
相关信息