17MnNiVNbR钢焊接接头的性能
Properties of 17MnNiVNbR Steel Welded Joints
摘 要
用电弧焊和埋弧焊对17MnNiVNbR钢板进行了对接焊, 并对焊接接头进行拉伸、冲击、落锤及裂纹尖端张开位移试验, 用光学显微镜观察了焊缝和热影响区的显微组织。结果表明: 焊后经(570±15) ℃×1 h热处理后, 焊接接头综合性能优良, 可满足国标的要求; 焊缝组织由先共析铁素体、针状铁素体和颗粒状贝氏体组成, 粗晶热影响区组织为粗大的贝氏体。
焊接接头
性能
17MnNiVNbR steel
welded joint
property
Abstract
17MnNiVNbR steel plates were welded by means of SMAW and SAW, and tensile, impact, drop-weight and the crack tip opening displacement (CTOD) tests were operated on welded joints. The microstructure of weld seam and heat affected zones (HAZ) was investigated by optical microscopy. The results show that welded joints after (570±15) ℃×1 h heat treatment had excellent comprehensive mechannical properties and could reach the GB requirement. Microstructure of weld seam consisted of proeutectoid ferrite, acicular ferrite and granular bainite, and microstructure of heat affected zone was coarse bainite.
中图分类号 TQ053.2
所属栏目
基金项目
收稿日期 2010/6/14
修改稿日期 2010/12/1
网络出版日期
作者单位点击查看
备注王利(1972-), 男, 安徽砀山人, 工程师, 硕士。
引用该论文: WANG Li,ZHANG Xiao-hu,GU Xian-shan,LI Shu-rui,DING Qing-feng. Properties of 17MnNiVNbR Steel Welded Joints[J]. Materials for mechancial engineering, 2011, 35(6): 65～67
王利,章小浒,顾先山,李书瑞,丁庆丰. 17MnNiVNbR钢焊接接头的性能[J]. 机械工程材料, 2011, 35(6): 65～67
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈晓, 秦晓钟.高性能压力容器和压力钢管用钢[M].北京: 机械工业出版社, 2007.
【2】许强, 王利, 徐亮, 等.汽车罐车罐体用WH590(17MnNiVNbR)钢的开发和试验研究[J].压力容器, 2010, 27(3):7-12.
【3】窦万波.特大型天然气球罐用WEL-TEN610CF钢板的冲击与断裂性能[J].机械工程材料, 2007, 31(6):59-62.
【2】许强, 王利, 徐亮, 等.汽车罐车罐体用WH590(17MnNiVNbR)钢的开发和试验研究[J].压力容器, 2010, 27(3):7-12.
【3】窦万波.特大型天然气球罐用WEL-TEN610CF钢板的冲击与断裂性能[J].机械工程材料, 2007, 31(6):59-62.
相关信息