Microstructure and Mechanical Properties of Transition Matched Welded Joints of 14NiCrMo10 6V and Q345E Steel
摘 要
采用E551T1-Ni2药芯焊丝对Q345E钢与14NiCrMo10 6V钢进行焊接, 并通过室温拉伸、弯曲、冲击、硬度试验以及金相分析等对焊接接头的力学性能与显微组织进行了研究。结果表明: 采用此焊丝可以获得拉伸、弯曲和冲击性能均良好的焊接接头, 焊缝硬度在200~250 HV之间; 焊缝处晶界组织为先共析铁素体、少量无碳贝氏体(从晶界伸向晶内), 晶内为针状铁素体与珠光体, 个别部位有粒状贝氏体; Q345E钢侧热影响区与焊缝过渡区的组织为沿晶界析出的块状先共析铁素体和向晶内生长的条状铁素体以及少量的珠光体和贝氏体; 14NiCrMo10 6V钢侧热影响区与焊缝过渡区的组织为板条状马氏体。
Abstract
E551T1-Ni2 flux cored wire was used to weld the steels between Q345E and 14NiCrMo10 6V, and then the mechanical properties and microstructure of the welded joints were studied through room temperature tensile, bending, impact and hardness tests as well as metallography analysis. The results show that welded joints with good tensile property, bending property and impact toughness could be obtained using the flux cored wire; the hardness of the weld seam was in the range of 200-250 HV. The microstructure at the grain boundaries in the weld seam was pre-eutectoid ferrite, a little carbon-free bainite which stretched from grain boundaries into the grains, and acicular ferrite and pearlite in the grains, also some granular bainite distributed at individual locations. The microstructure of heat affected zone (HAZ) and weld seam transition area at the side of Q345E steel consisted mainly of block pre-eutectoid ferrite which precipitated along the grain boundaries, and some lath ferrite which stretched into the grains, and small amount pearlite and bainite. While the microstructure of HAZ and weld seam transition area at the side of 14NiCrMo10 6V steel was lath martensite and granular bainite.
中图分类号 TG457
所属栏目 试验研究
基金项目
收稿日期 2011/3/20
修改稿日期 2011/11/11
网络出版日期
作者单位点击查看
备注蒋立明(1963-), 男, 辽宁抚顺人, 高级工程师, 学士。
引用该论文: JIANG Li-ming,ZHENG Hua-yong,XU Hong-ji,XIE Ming. Microstructure and Mechanical Properties of Transition Matched Welded Joints of 14NiCrMo10 6V and Q345E Steel[J]. Materials for mechancial engineering, 2012, 36(2): 37~39
蒋立明,郑华勇,许鸿吉,谢明. 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能[J]. 机械工程材料, 2012, 36(2): 37~39
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】潘春旭.异种钢及异种金属焊接[M].北京:人民交通出版社, 2000.
【2】王国凡.钢结构焊接制造[M].北京:化学工业出版社, 2009.
【3】中国机械工程学会焊接学会.焊接手册(焊接材料) [M]. 北京:机械工业出版社, 1992.
【4】吕德林.焊接金相分析[M].北京:机械工业出版杜, 1986.
【5】陈裕川.低合金结构钢的焊接[M].北京:机械工业出版社, 1992.
【2】王国凡.钢结构焊接制造[M].北京:化学工业出版社, 2009.
【3】中国机械工程学会焊接学会.焊接手册(焊接材料) [M]. 北京:机械工业出版社, 1992.
【4】吕德林.焊接金相分析[M].北京:机械工业出版杜, 1986.
【5】陈裕川.低合金结构钢的焊接[M].北京:机械工业出版社, 1992.
相关信息