In-situ Synthesis of ZrB2/A356 Composites under High-Intensity Ultrasonic and Its Wear Property
摘 要
以Al-K2ZrF6-KBF4为反应体系, 在高能超声下原位合成了ZrB2/A356复合材料; 研究了超声功率对ZrB2颗粒尺寸、形貌、分布的影响, 以及复合材料室温干滑动磨损性能。结果表明: 随着超声功率的增加, 复合材料中的ZrB2颗粒逐渐细化, 其含量也有一定程度提高; 当超声功率达到1.6 kW时, 出现大量ZrB2纳米颗粒, 其形貌由原来的块状、柱状变为粒状, 复合材料的磨损量减小到56 mg, 耐磨性提高到1.08, 磨损面出现较明显的犁沟。
Abstract
The ZrB2/A356 composite was in-situ synthetized from Al-K2ZrF6-KBF4 reaction system under high-intensity ultrasonic. The effect of ultrasonic power on ZrB2particle size, morphology and distribution was studied and the dry sliding wear property of the composite at room temperature was studied, too. The results show that the size of ZrB2 particles were fined gradually and the content of ZrB2 particles rose with the increase of ultrasonic power in certain degree. There are amounts of ZrB2 particles were found, the morphology of particles changed into granular from block and columnar, the wear loss decreased to 56 mg and the resistant wear increased to 1.08, and obvious furrows appeared on wear surface when the ultrasonic power was 1.6 kW.
中图分类号 TG146.2
所属栏目 材料性能及其应用
基金项目 国家自然科学基金资助项目(50971066)
收稿日期 2011/3/15
修改稿日期 2011/12/18
网络出版日期
作者单位点击查看
备注祝海燕(1980-),女,山东菏泽人, 硕士。
引用该论文: ZHU Hai-yan,ZHAO Yu-tao,WANG Hong-lei,CHEN Deng-bin. In-situ Synthesis of ZrB2/A356 Composites under High-Intensity Ultrasonic and Its Wear Property[J]. Materials for mechancial engineering, 2012, 36(3): 62~64
祝海燕,赵玉涛,王洪磊,陈登斌. 高能超声下原位合成ZrB2/A356复合材料及其磨损性能[J]. 机械工程材料, 2012, 36(3): 62~64
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】ZAWRAH M F, ALY M H. In situ formation of Al2O3-SiC mullite from Al-matrix composites[J].Ceramics International,2006,32(1):21-28.
【2】KUMAR S, CHAKRABORTY M, SARMA V S, et al. Tensile and wear behaviour of in situ Al-7Si/TiB2 particulate composites[J].Wear,2008,265:134-142.
【3】FAN Tong-xiang, ZHANG Di, YANG Guang, et al. Fabrication of in situ Al2O3/Al composite via remelting[J].Journal of Materials Processing Technology,2003,142:556-561.
【4】WANG Hai-long, ZHANG Rui, HU Xing, et al. Characterization of a powder metallurgy SiC/Cu-Al composite[J].Journal of Materials Processing Technology,2008,197:43-48.
【5】TANI T. Processing, microstructure and properties of in-situ reinforced SiC matrix composites[J].Composites Part A,1999,30:419-423.
【6】余志勇,郝斌,崔华,等.纳米SiC颗粒增强铝基复合材料制备工艺进展[J].材料导报,2006,20(增刊):206-208.
【7】CAMURLU H E, MAGLIA F. Preparation of nano-size ZrB2 powder byself-propagating high-temperature synthesis[J].Journal of the European Ceramic Society,2009,29:1501-1506.
【8】张松利, 赵玉涛, 陈刚, 等.超声化学原位合成(Al3Zr+ZrB2)/A356复合材料的力学行为[J].有色金属学报,2008,18(12):2140-2144.
【9】刘磊,赵玉涛,贾志宏,等.超声化学原位合成ZrB2/A356复合材料的微观组织和力学性能[J].材料热处理技术,2010,39(11):98-101.
【10】FJELLSTEDT J, JARFORS A E W. On the precipitation of TiB2 in aluminum melts from the reaction with KBF4 and K2TiF6[J].Materials Science and Engineering A,2005,413/414:527-532.
【11】王俊,陈锋,孙宝德.高能超声在制备颗粒增强金属基复合材料中的作用[J].上海交通大学学报,1999,3(7):813-816.
【12】陶杰,赵玉涛,潘蕾,等.金属基复合材料制备新技术导论[M].北京:化学工业出版社,2007.
【13】陈跃,邢建东,张永振,等.增强颗粒对铝基复合材料摩擦学性能的影响[J].摩擦学学报,2001,21(4):251-255.
【2】KUMAR S, CHAKRABORTY M, SARMA V S, et al. Tensile and wear behaviour of in situ Al-7Si/TiB2 particulate composites[J].Wear,2008,265:134-142.
【3】FAN Tong-xiang, ZHANG Di, YANG Guang, et al. Fabrication of in situ Al2O3/Al composite via remelting[J].Journal of Materials Processing Technology,2003,142:556-561.
【4】WANG Hai-long, ZHANG Rui, HU Xing, et al. Characterization of a powder metallurgy SiC/Cu-Al composite[J].Journal of Materials Processing Technology,2008,197:43-48.
【5】TANI T. Processing, microstructure and properties of in-situ reinforced SiC matrix composites[J].Composites Part A,1999,30:419-423.
【6】余志勇,郝斌,崔华,等.纳米SiC颗粒增强铝基复合材料制备工艺进展[J].材料导报,2006,20(增刊):206-208.
【7】CAMURLU H E, MAGLIA F. Preparation of nano-size ZrB2 powder byself-propagating high-temperature synthesis[J].Journal of the European Ceramic Society,2009,29:1501-1506.
【8】张松利, 赵玉涛, 陈刚, 等.超声化学原位合成(Al3Zr+ZrB2)/A356复合材料的力学行为[J].有色金属学报,2008,18(12):2140-2144.
【9】刘磊,赵玉涛,贾志宏,等.超声化学原位合成ZrB2/A356复合材料的微观组织和力学性能[J].材料热处理技术,2010,39(11):98-101.
【10】FJELLSTEDT J, JARFORS A E W. On the precipitation of TiB2 in aluminum melts from the reaction with KBF4 and K2TiF6[J].Materials Science and Engineering A,2005,413/414:527-532.
【11】王俊,陈锋,孙宝德.高能超声在制备颗粒增强金属基复合材料中的作用[J].上海交通大学学报,1999,3(7):813-816.
【12】陶杰,赵玉涛,潘蕾,等.金属基复合材料制备新技术导论[M].北京:化学工业出版社,2007.
【13】陈跃,邢建东,张永振,等.增强颗粒对铝基复合材料摩擦学性能的影响[J].摩擦学学报,2001,21(4):251-255.
相关信息