发动机排气阀的开裂原因
Cracking Causes of Evacuation Valves of an Engine
摘 要
对开裂的发动机排气阀的宏观形貌、显微组织、晶粒度、化学成分、硬度、断口形貌以及腐蚀产物相组成进行研究, 并对其开裂原因进行了分析。结果表明: 排气阀的开裂为疲劳断裂; 疲劳裂纹源位于堆焊层中, 由于堆焊工艺操作不当造成显微孔洞; 排气阀的堆焊层中及阀基体的固溶体晶界处存在大量碳化物, 导致其性能严重下降, 在工作载荷的作用下裂纹很容易自显微孔洞处扩展最终形成开裂; 腐蚀产物主要为氧化锌、磷酸盐和硫酸盐类等。
腐蚀
断口形貌
开裂
engine evacuation valve
corrosion
fracture morphology, cracking
Abstract
The macrophotoes, microstructure, grain size, chemical composition, hardness, fracture morphology and phase composition of corrosion products for cracked evacuation valves of an engine were studied and the cracking causes were analyzed . The results show that the cracking of evacuations valve was fatigue cracking and the fatigue crack sources were in the cladding layer, and the microholes caused by improper cladding process. A lot of carbides, which were found in cladding layer of evacuation valves and the grains boundaries of solid solution in the valve matrix, made the properties decrease seriously. Cracks easily extended from microvoids and fracture at last. Corrosion products mainly were ZnO, phosphate, sulfate and so on.
中图分类号 TE988
所属栏目 失效分析
基金项目
收稿日期 2011/2/21
修改稿日期 2011/12/8
网络出版日期
作者单位点击查看
备注薛小强(1973-), 男, 甘肃天水人, 工程师, 学士。
引用该论文: XUE Xiao-qiang,SONG Wen-ming,LIU Ting-ting,YANG Gui-rong,ZHONG Yan-ping. Cracking Causes of Evacuation Valves of an Engine[J]. Materials for mechancial engineering, 2012, 36(3): 101～104
薛小强,宋文明,刘婷婷,杨贵荣,钟彦平. 发动机排气阀的开裂原因[J]. 机械工程材料, 2012, 36(3): 101～104
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡光立.钢的热处理(原理和工艺)[M].西安: 西北工业大学出版社,1993.
【2】李炯辉,施友方,高汉文. 钢铁材料金相图谱[M].上海: 上海科学技术出版社,1981.
【3】崔约贤.金属断口分析[M]. 哈尔滨: 哈尔滨工业大学出版社,1998.
【2】李炯辉,施友方,高汉文. 钢铁材料金相图谱[M].上海: 上海科学技术出版社,1981.
【3】崔约贤.金属断口分析[M]. 哈尔滨: 哈尔滨工业大学出版社,1998.
相关信息