Microstructure and Tribology Property of Plasma Nickelized Alloy Layer on Pure Titanium Surface
摘 要
采用等离子表面合金化技术对纯钛进行表面渗镍处理, 对渗镍后形成的合金层显微组织、物相组成及硬度进行了分析, 并对其摩擦学性能进行了研究。结果表明: 渗镍后在纯钛表面形成了与基体结合良好的钛-镍合金层, 合金层主要由Ti2Ni、TiNi及钛相组成, 厚约30 μm, 显微硬度约为570 HV, 合金层的干滑动摩擦磨损性能较纯钛基体的有很大提高。
Abstract
Plasma surface alloying technology was applied to nickelizing on pure titanium surface. The microstructure, phase and hardness of the alloy layer formed after nickelizing were analyzed, and the tribology property of the alloy layer was studied. The results show that the Ti-Ni alloy layer with a thickness of about 30 μm was well bonded with pure titanium substrate and mainly consisted of Ti2Ni, TiNi and Ti phases. The microhardness of the alloy layer was about 570 HV. The dry sliding friction and wear property of the alloy layer was improved obviously comparing with that of pure titanium substrate.
中图分类号 TG146.1
所属栏目 材料性能及其应用
基金项目 国家自然科学基金资助项目(51071106, 50671071); 太原市科技项目计划明星专项(08121030); 山西省留学基金资助项目(2008-38)
收稿日期 2011/3/29
修改稿日期 2011/12/10
网络出版日期
作者单位点击查看
备注王泽莹(1987-), 女, 山西运城人, 硕士研究生。
引用该论文: WANG Ze-ying,ZHANG Feng,WANG Zhen-xia,HE Zhi-yong,LIU Xiao-ping,TANG Bin. Microstructure and Tribology Property of Plasma Nickelized Alloy Layer on Pure Titanium Surface[J]. Materials for mechancial engineering, 2012, 36(4): 73~76
王泽莹,张峰,王振霞,贺志勇,刘小萍,唐宾. 纯钛表面等离子渗镍合金层的显微组织及摩擦学性能[J]. 机械工程材料, 2012, 36(4): 73~76
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘凤玲, 李金桂, 冯自修.钛合金表面技术的进展[J].腐蚀与防护, 2001, 22(2): 54-57.
【2】蔡珣.等离子体基离子注入技术发展及其应用[J].机械工人, 2005(4): 33-35.
【3】李启全, 祁珊.NiTi形状记忆合金超弹性的研究进展[J].国外金属热处理, 2003, 24(4): 5-9.
【4】XU Z, GAO Y.Plasma surface metallurgy technology[J].Journal of Advanced Materials, 2002, 34(3): 32-38.
【5】IU X P, XU Z, WU W, et al. Plasma surface alloying with molybdenum and carburization of TiAl based alloys [J].Trans Nonferrous Met Soc China, 2005, 15(3): 420-424.
【6】ZHANG X, XU Z. A study of nickel-based corrosion resisting alloy layer obtained by double glow plasma surface alloying technique[J].Surface Coatings and Technology, 2003, 131: 378-382.
【7】秦林, 唐宾, 刘道新, 等.钛合金Ti6Al4V表面Mo-N改性层的摩擦性能研究[J].稀有金属材料与工程, 2005, 34(9): 1466-1468.
【8】JIN J, WANG H. Wear resistance of Ni-Ti alloy[J].Acta Metall Sinica, 1988, 66: 76-81.
【9】YU J Q. Handbook of binary alloy phase diagrams[M].Shanghai: Science and Technology Pubishing Company, 1987.
【10】GAO F, WANG H M. Drying sliding wear property of a laser melting/deposited Ti2Ni/TiNi intermetallic alloy[J].Intermetallics, 2008, 16: 202-208.
【11】LI C J, XU Z. Diffusion mechanism of lon bombardment [J].Surface Engineering, 1987(4): 310-312.
【12】张平则, 徐重, 张高辉, 等.纯Ti及Ti6Al4V双层辉光离子渗Mo[J].南京航空航天大学学报, 2005(5): 583-586.
【13】徐恒钧.材料科学基础[M].北京: 北京工业大学出版社, 2001.
【14】刘家浚. 材料磨损原理及其耐磨性[M].北京: 清华大学出版社, 1993.
【15】徐重.等离子表面冶金学[M].北京: 科学出版社, 2008.
【2】蔡珣.等离子体基离子注入技术发展及其应用[J].机械工人, 2005(4): 33-35.
【3】李启全, 祁珊.NiTi形状记忆合金超弹性的研究进展[J].国外金属热处理, 2003, 24(4): 5-9.
【4】XU Z, GAO Y.Plasma surface metallurgy technology[J].Journal of Advanced Materials, 2002, 34(3): 32-38.
【5】IU X P, XU Z, WU W, et al. Plasma surface alloying with molybdenum and carburization of TiAl based alloys [J].Trans Nonferrous Met Soc China, 2005, 15(3): 420-424.
【6】ZHANG X, XU Z. A study of nickel-based corrosion resisting alloy layer obtained by double glow plasma surface alloying technique[J].Surface Coatings and Technology, 2003, 131: 378-382.
【7】秦林, 唐宾, 刘道新, 等.钛合金Ti6Al4V表面Mo-N改性层的摩擦性能研究[J].稀有金属材料与工程, 2005, 34(9): 1466-1468.
【8】JIN J, WANG H. Wear resistance of Ni-Ti alloy[J].Acta Metall Sinica, 1988, 66: 76-81.
【9】YU J Q. Handbook of binary alloy phase diagrams[M].Shanghai: Science and Technology Pubishing Company, 1987.
【10】GAO F, WANG H M. Drying sliding wear property of a laser melting/deposited Ti2Ni/TiNi intermetallic alloy[J].Intermetallics, 2008, 16: 202-208.
【11】LI C J, XU Z. Diffusion mechanism of lon bombardment [J].Surface Engineering, 1987(4): 310-312.
【12】张平则, 徐重, 张高辉, 等.纯Ti及Ti6Al4V双层辉光离子渗Mo[J].南京航空航天大学学报, 2005(5): 583-586.
【13】徐恒钧.材料科学基础[M].北京: 北京工业大学出版社, 2001.
【14】刘家浚. 材料磨损原理及其耐磨性[M].北京: 清华大学出版社, 1993.
【15】徐重.等离子表面冶金学[M].北京: 科学出版社, 2008.
相关信息