7075铝合金缸体的失效分析
Failure Analysis for 7075 Aluminum Alloy Cylinder
摘 要
对在工作中发生断裂的7075铝合金缸体进行了化学成分分析、室温拉伸试验和断口形貌分析, 以找到其失效的原因, 给出相应的改进措施。结果表明: 镁元素含量低于标准导致合金力学性能降低是该铝合金缸体失效的主要原因; 阳极氧化膜上的微孔在循环应力作用下沿着机加工痕迹扩展形成疲劳源; 随着应力循环的加剧, 裂纹快速扩展, 最终使缸体发生疲劳断裂。
断口形貌
失效分析
7075 aluminum alloy
fracture morphology
failure analysis
Abstract
The 7075 aluminum alloy cylinder fractured during work, and then was analyzed through chemical composition, room temperature tensile test and fracture morphology to find the fracture reasons, and the relevant improved methods were proposed. The results show that the main reason for the aluminum alloy cylinder fracture was the mechanical property of the alloy decreasing because content of Mg was below the standard content. The micropore on oxide film extended along machining mark to cause fatigue source forning under cyclic stress, the crack extended quickly as the stress circulation intensify, and the fatigue fracture for 7075 aluminum alloy cylinder happened at last.
中图分类号 TG142.73
所属栏目 失效分析
基金项目 国家重点基础研究发展计划资助项目(2005CB623705-04)
收稿日期 2011/5/28
修改稿日期 2011/10/28
网络出版日期
作者单位点击查看
备注姜伟(1982-), 男, 宁夏银川人, 工程师, 硕士。
引用该论文: JIANG Wei,DUAN An-jing. Failure Analysis for 7075 Aluminum Alloy Cylinder[J]. Materials for mechancial engineering, 2012, 36(6): 94～96
姜伟,段安婧. 7075铝合金缸体的失效分析[J]. 机械工程材料, 2012, 36(6): 94～96
被引情况:
【1】陈灿龙,李建亮,孔见, "6N01铝合金中厚板三点弯曲变形行为的数值模拟",机械工程材料 40, 59-64(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邱惠中, 吴志红.航天用高性能金属材料的新进展[J].宇航材料工艺, 1996(2): 18-25.
【2】刘宏, 赵刚, 刘春明, 等.6000系铝合金组织性能的研究进展[J].机械工程材料, 2004, 28(6): 1-5.
【3】曾渝, 尹志民, 潘青林, 等.超高强铝合金的研究现状及发展趋势[J].中南工业大学学报, 2002, 33(6): 592-563.
【4】吴安如, 戴晓元, 夏长青.微量银对Al-Zn-Mg-Cu系合金微观组织和力学性能的影响[J].机械工程材料, 2005, 29(12): 42-46.
【2】刘宏, 赵刚, 刘春明, 等.6000系铝合金组织性能的研究进展[J].机械工程材料, 2004, 28(6): 1-5.
【3】曾渝, 尹志民, 潘青林, 等.超高强铝合金的研究现状及发展趋势[J].中南工业大学学报, 2002, 33(6): 592-563.
【4】吴安如, 戴晓元, 夏长青.微量银对Al-Zn-Mg-Cu系合金微观组织和力学性能的影响[J].机械工程材料, 2005, 29(12): 42-46.
相关信息