Microstructure and Microhardness of TiC Particles Reinforced Coating In-situ Deposited on Titanium Alloy Surface by Electrospark Process
摘 要
以石墨为电极, 采用电火花沉积工艺在BT20钛合金表面沉积了TiC颗粒得到了强化层, 并对该强化层的组织和硬度进行了研究。结果表明: 强化层分布不连续, 厚度也不均匀, 最厚处可达30 μm, 最薄处还不到10 μm; 强化层中TiC颗粒的分布不均匀, 大量TiC聚集于强化层表面, 内部很少, 这使得强化层表面硬度达到了基体的5倍以上。
Abstract
Taking the graphite as electrode, TiC particles were deposited on BT20 titanium alloy surface by eletrospark processing to form a reinforced coating. The microstructure and microhardness of the coating were studied. The results show that the coating was discontinuous and uneven with the thickness of 10-30 μm. The distribution of TiC particles in the reinforced coating was non-uniform, most of TiC existed on the reinforced coating surface and a little inside of the reinforced coating, which made the microhardness of the reinforced coating 4 times higher than that of the titanium alloy substrate.
中图分类号 TG135.6
所属栏目 试验研究
基金项目
收稿日期 2011/11/16
修改稿日期 2012/7/30
网络出版日期
作者单位点击查看
备注王忠英(1954-), 女, 山东烟台人, 副教授, 学士。
引用该论文: WANG Zhong-ying,PANG Yong-ping,WANG Kun. Microstructure and Microhardness of TiC Particles Reinforced Coating In-situ Deposited on Titanium Alloy Surface by Electrospark Process[J]. Materials for mechancial engineering, 2012, 36(12): 25~27
王忠英,庞永平,王坤. 钛合金表面电火花原位沉积TiC颗粒强化层的组织与硬度[J]. 机械工程材料, 2012, 36(12): 25~27
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郝建军,黄继华,周志军,等.钛合金表面反应电火花沉积Ti(CN)涂层研究[J]. 材料热处理学报,2008,29(2):128-130.
【2】BE JAR M A, SCHNAKE W, SAAVEDRA W,et al.Surface hardening of metallic alloys by electrospark deposition followed by plasma nitriding[J]. Journal of Materials Processing Technology, 2006, 176: 210-213.
【3】王振廷,陈丽丽,张显友.钛合金表面氩弧熔覆TiC增强复合涂层组织与性能分析[J]. 焊接学报,2008,29(9):43-45.
【4】朱警雷,黄继华,王海涛,等.反应等离子喷涂TiC/Fe-Ni金属陶瓷复合涂层的显微组织[J]. 中国有色金属学报,2008,18(1):36-41.
【5】ZHANG G J, BEPPU Y, OHJI T,et al.Reaction mechanism and microstructure development of strain tolerant in-situ SiC-BN composites[J]. Acta Materials,2001,49(1): 77-82.
【6】FENINECHE N, KEDIM O E, CODDET C. The effect of pulse parameters on the electrodeposition of Co-Ni alloy[J]. Surface and Coatings Technology,1991,48:205-209.
【7】陈钟燮. 电火花表面强化工艺[M]. 北京:机械工业出版社,1987.
【8】张维平,冯新. 45钢表面电火花沉积强化层的组织与性能[J]. 机械工程材料,2008,32(1):73-75.
【9】牛静,张立文,张全忠,等. BT20钛合金电火花沉积TiC涂层的微观组织研究[J]. 金属热处理,2006,31(4):59-61.
【10】郝建军,彭海滨,黄继华,等.钛合金表面反应电火花沉积TiN/Ti复合涂层[J]. 焊接学报,2009,30(11): 69-72.
【11】杨黎明.刀具设计手册[M]. 北京:兵器工业出版社,1998:17-18.
【12】罗成,董仕节,熊翔,等.45钢表面电火花沉积TiB2涂层的结构及性能[J]. 机械工程材料,2009,33(11):54-57.
【13】王世杰,傅博.电火花表面强化的试验与研究[J]. 辽宁工学院学报,1999,19 (3):8-11.
【2】BE JAR M A, SCHNAKE W, SAAVEDRA W,et al.Surface hardening of metallic alloys by electrospark deposition followed by plasma nitriding[J]. Journal of Materials Processing Technology, 2006, 176: 210-213.
【3】王振廷,陈丽丽,张显友.钛合金表面氩弧熔覆TiC增强复合涂层组织与性能分析[J]. 焊接学报,2008,29(9):43-45.
【4】朱警雷,黄继华,王海涛,等.反应等离子喷涂TiC/Fe-Ni金属陶瓷复合涂层的显微组织[J]. 中国有色金属学报,2008,18(1):36-41.
【5】ZHANG G J, BEPPU Y, OHJI T,et al.Reaction mechanism and microstructure development of strain tolerant in-situ SiC-BN composites[J]. Acta Materials,2001,49(1): 77-82.
【6】FENINECHE N, KEDIM O E, CODDET C. The effect of pulse parameters on the electrodeposition of Co-Ni alloy[J]. Surface and Coatings Technology,1991,48:205-209.
【7】陈钟燮. 电火花表面强化工艺[M]. 北京:机械工业出版社,1987.
【8】张维平,冯新. 45钢表面电火花沉积强化层的组织与性能[J]. 机械工程材料,2008,32(1):73-75.
【9】牛静,张立文,张全忠,等. BT20钛合金电火花沉积TiC涂层的微观组织研究[J]. 金属热处理,2006,31(4):59-61.
【10】郝建军,彭海滨,黄继华,等.钛合金表面反应电火花沉积TiN/Ti复合涂层[J]. 焊接学报,2009,30(11): 69-72.
【11】杨黎明.刀具设计手册[M]. 北京:兵器工业出版社,1998:17-18.
【12】罗成,董仕节,熊翔,等.45钢表面电火花沉积TiB2涂层的结构及性能[J]. 机械工程材料,2009,33(11):54-57.
【13】王世杰,傅博.电火花表面强化的试验与研究[J]. 辽宁工学院学报,1999,19 (3):8-11.
相关信息