轴承钢大颗粒夹杂物的高频超声波C型扫描检测
Test of Large Inclusions in Bearing Steel by High Frequence Ultrasonic C-scan
摘 要
大颗粒夹杂物对轴承钢的疲劳寿命有重大的影响。针对轴承钢非金属夹杂物的评价方法进行了比较和分析。利用高频超声波C型扫描法对轴承钢钢材试样进行检测,并利用金相法对超声波C型扫描法检测的结果进行验证。结果表明:高频超声波C型扫描法用于检测轴承钢中的大颗粒夹杂物是非常有效的。
大颗粒夹杂物
高频超声波C型扫描
bearing steel
large inclusions
high frequence ultrasonic C-scan
Abstract
Large inclusions have a significant impact on the fatigue life of bearing steel.The evaluationmethods for inclusions in bearing steel were compared and analyzed.Bearing steel were tested by high frequenceultrasonic C-scan,and using metallographic method to validate the results.The results showed that the testingmethod of high frequence ultrasonic C-scan was effective for the testing of large inclusions in bearing steel.
中图分类号 TG115.28+5 TG115.21
所属栏目 试验技术与方法
基金项目
收稿日期 2010/9/25
修改稿日期
网络出版日期
作者单位点击查看
备注杨娥(1984-),女,工程师,硕士。
引用该论文: YANG E,ZHOU Li-xin,LIU Guang-hui,GAO Lin,CHEN Jia-xin,DU Dao-jing. Test of Large Inclusions in Bearing Steel by High Frequence Ultrasonic C-scan[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(1): 30～32
杨娥,周立新,刘光辉,高林,陈家新,杜道京. 轴承钢大颗粒夹杂物的高频超声波C型扫描检测[J]. 理化检验－物理分册, 2011, 47(1): 30～32
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】栾燕.新编国外轴承钢标准汇编[M].[s.l.]:[s.n.],1999:462-469.
【2】GB/T 18254-2002 高碳铬轴承钢[S].
【3】GB/T 10561-2005 钢中非金属夹杂物含量的测定标准评级图显微检验法[S].
【4】李克明.超声波探伤[M].北京:电力工业出版社,1980.
【5】ASTM E588-2003 用超声波法检测轴承钢中大块夹杂物的标准实施规范[S].
【2】GB/T 18254-2002 高碳铬轴承钢[S].
【3】GB/T 10561-2005 钢中非金属夹杂物含量的测定标准评级图显微检验法[S].
【4】李克明.超声波探伤[M].北京:电力工业出版社,1980.
【5】ASTM E588-2003 用超声波法检测轴承钢中大块夹杂物的标准实施规范[S].
相关信息