Q345E热轧中厚板探伤不合格原因分析
Unqualified Reason Analysis on Non-destructure Testing ofQ345E Hot Rolling Medium Plate
摘 要
通过低倍检验、金相检验和断口分析等方法分析了Q345E热轧中厚板探伤不合格的原因。结果表明:探伤不合格的原因是在热轧板中心区域偏析带存在硫化锰和碳氮化铌夹杂物,并通过控制和调整工艺解决了该问题。
超声波探伤
夹杂物
偏析
hot rolling medium plate
ultrasonic inspection
inclusions
segregation
Abstract
The unqualified reason of Q345E hot rolling medium plate by ultrasonic inspection had beenanalyzed by means of macroscopic examination,metallographic examination,fracture analysis and so on.The resultsshowed that the reason was the segregation zone and the inclusions including manganese sulfide and niobiumcarbonitride which congregated in the central part of the medium plate.And the problem was solved by adjusting theprocess.
中图分类号 TG115.28+5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2010/2/25
修改稿日期
网络出版日期
作者单位点击查看
备注李智丽(1971-),女,高级工程师,硕士。
引用该论文: LI Zhi-li. Unqualified Reason Analysis on Non-destructure Testing ofQ345E Hot Rolling Medium Plate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(1): 53～56
李智丽. Q345E热轧中厚板探伤不合格原因分析[J]. 理化检验－物理分册, 2011, 47(1): 53～56
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】韩炯,高亮.Q345qE钢板探伤缺陷原因分析[J].物理测试,2006,24(3):42-45.
【2】陆岳璋,熊晓伟.中厚钢板探伤缺陷的研究[J].冶金分析,2004,24(增刊): 650-655.
【2】陆岳璋,熊晓伟.中厚钢板探伤缺陷的研究[J].冶金分析,2004,24(增刊): 650-655.
相关信息