102钢的显微组织形态与室温力学性能的关系
Relation between Microstructure and Room Temperature Mechanical Properties of 102 Steel
摘 要
对若干具备正常或老化组织形态的102钢试样进行室温抗拉强度和硬度试验,研究了组织形态与力学性能的关系。结果表明:正常组织形态的试样的室温抗拉强度和硬度偏标准上限,随着组织老化级别的提高,室温抗拉强度和硬度降低,组织老化达到4级时,室温抗拉强度和硬度已接近标准下限。
显微组织
室温抗拉强度
硬度
102 steel
microstructure
room temperature tensile strength
hardness
Abstract
The relation between microstructure and mechanical properties of 102 steel was studied by room temperature tensile strength and hardness test of some 102 steel samples with normal or aging microstructure. The results showed that room temperature tensile strength and hardness of the samples with normal microstructure could reach the standard maximum. Mechanical properties would become lower with the aging of microstructure. When aging achieved the four level, mechanical properties had closed to the standard minimum.
中图分类号 TG142.1
所属栏目 试验与研究
基金项目
收稿日期 2010/9/9
修改稿日期
网络出版日期
作者单位点击查看
备注赵永峰(1979-),男,工学硕士。
引用该论文: ZHAO Yong-feng,XU Jiang-xiao,LI Shi-tao. Relation between Microstructure and Room Temperature Mechanical Properties of 102 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(3): 143～145
赵永峰,许江晓,李世涛. 102钢的显微组织形态与室温力学性能的关系[J]. 理化检验－物理分册, 2011, 47(3): 143～145
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李金峰,欧阳杰.102钢老化后力学性能变化规律[J]. 河北电力技术,1996(3):10-14.
【2】冶金部钢铁研究院102钢专题组.102钢的合金化问题及显微组织[J].新金属材料,1978(4):1-5.
【3】刘荣藻.低合金热强钢的强化机理[M].北京:冶金工业出版社,1981.
【4】周颐深.低合金耐热钢[M].上海:上海人民出版社,1976.
【5】冯砚厅,孙彦.102钢热影响区内碳化物析出规律的初步研究[J].电力建设,1999(8):8-11.
【6】沈非,郑国,张雪,等.12Cr2MoWVTiB钢服役过程中组织与性能变化研究[J].理化检验-物理分册,2001,37(11):466-469.
【2】冶金部钢铁研究院102钢专题组.102钢的合金化问题及显微组织[J].新金属材料,1978(4):1-5.
【3】刘荣藻.低合金热强钢的强化机理[M].北京:冶金工业出版社,1981.
【4】周颐深.低合金耐热钢[M].上海:上海人民出版社,1976.
【5】冯砚厅,孙彦.102钢热影响区内碳化物析出规律的初步研究[J].电力建设,1999(8):8-11.
【6】沈非,郑国,张雪,等.12Cr2MoWVTiB钢服役过程中组织与性能变化研究[J].理化检验-物理分册,2001,37(11):466-469.
相关信息