外压型不锈钢波纹管膨胀节开裂分析
Cracking Analysis of External Pressure Stainless Steel Bellows Expansion-joint
摘 要
奥氏体不锈钢外压轴向型波纹管膨胀节在使用较短时间后发生了开裂。采用化学成分分析、金相检验和断口分析等方法对开裂的原因进行了分析。结果表明:波纹管膨胀节的工作介质过热蒸汽中含有腐蚀性氯离子,在服役环境下受到拉伸应力的作用,导致其发生了应力腐蚀开裂。
奥氏体不锈钢
应力腐蚀开裂
bellows expansion-joint
austenitic stainless steel
stress corrosion cracking
Abstract
External pressure axial type bellows expansion joint of austenitic stainless steel cracked after using for short time. The cracking reason was analyzed by means of chemical composition analysis, metallographic examination and fracture analysis. The results showed that superheated steam of working medium in the expansion-joint contained corrosive chloride ions, and the expansion-joint was affected by tensile stress, which resulted in stress corrosion cracking.
中图分类号 TG142.71
所属栏目 质量控制与失效分析
基金项目
收稿日期 2010/5/12
修改稿日期
网络出版日期
作者单位点击查看
备注李小东(1983-),男,硕士研究生。
引用该论文: LI Xiao-dong,HAO Xi-yun,CHEN Jin,SUN Xiao-ming. Cracking Analysis of External Pressure Stainless Steel Bellows Expansion-joint[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(3): 187～188
李小东,郝习云,陈进,孙晓明. 外压型不锈钢波纹管膨胀节开裂分析[J]. 理化检验－物理分册, 2011, 47(3): 187～188
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙智.失效分析———基础与应用[M].北京:机械工业出版社,2005.
【2】肖纪美.应力作用下的金属腐蚀[M].北京:化学工业出版社,1990.
【3】郭海霞.小型锅炉锅筒开裂原因分析[J].理化检验-物理分册,2008,44(5):255-257.
【2】肖纪美.应力作用下的金属腐蚀[M].北京:化学工业出版社,1990.
【3】郭海霞.小型锅炉锅筒开裂原因分析[J].理化检验-物理分册,2008,44(5):255-257.
相关信息