电厂外供泵轴断裂原因分析
Fracture Reason Analysis of External Supply Pump Shaft in Power Plant
摘 要
某外供泵在运行期间其泵轴发生断裂。通过宏观和微观检验、化学成分分析以及硬度测试等方法对泵轴断裂的原因进行了分析。结果表明:该轴的热处理没有达到要求,使各项强度指标显著降低,加上在应力集中部位键槽根部产生了疲劳裂纹,并进一步扩展,最终导致泵轴断裂。
断裂
疲劳
应力集中
pump shaft
fracture
fatigue
stress concentration
Abstract
The shaft of external supply pump was fractured in use. The fracture reason was analyzed by means of macroscopic and microscopic examination, chemical composition analysis, hardness testing and so on. The results showed that the main fracture reason was the improper heat treatment process, which reduced the mechanical properties of shaft. Furthermore, the fatigue cracks initiated in the root of keyway which was stress concentration position, and the cracks extended further and further, the shaft was fractured at last.
中图分类号 TM621.7
所属栏目
基金项目
收稿日期 2010/9/7
修改稿日期
网络出版日期
作者单位点击查看
备注朱晏萱(1982-),女,助教,工学硕士。
引用该论文: ZHU Yan-xuan,BI Qi-iing,DING Yong-xiu. Fracture Reason Analysis of External Supply Pump Shaft in Power Plant[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(5): 312～314
朱晏萱,毕启玲,丁永秀. 电厂外供泵轴断裂原因分析[J]. 理化检验－物理分册, 2011, 47(5): 312～314
被引情况:
【1】孙明成,张轶昕, "脱硫氧化风机轴断裂原因分析",理化检验－物理分册 50, 929-932(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郑文龙.金属构件断裂分析与防护[M].上海:上海技术出版社,1980.
【2】王丽娟,张国福,宋天民,等.泵轴断裂原因分析[J]. 辽宁石油化工大学学报,2005,25(3):43-47.
【3】GB/T699-1999 优质碳素结构钢[S].
【4】成大先.机械设计手册[M].北京:化学工业出版社, 2004:1-377.
【5】朱宗元,李邦俊,李玉青.潜油电泵轴断裂失效分析[J].理化检验-物理分册,2000,36(1): 34-36.
【2】王丽娟,张国福,宋天民,等.泵轴断裂原因分析[J]. 辽宁石油化工大学学报,2005,25(3):43-47.
【3】GB/T699-1999 优质碳素结构钢[S].
【4】成大先.机械设计手册[M].北京:化学工业出版社, 2004:1-377.
【5】朱宗元,李邦俊,李玉青.潜油电泵轴断裂失效分析[J].理化检验-物理分册,2000,36(1): 34-36.
相关信息