集液器端盖爆破试验后开裂原因分析
Analysis on Cracking Cause of End Shield of Liquid Trap after Blast Experiment
摘 要
采用化学成分分析、宏观和微观检验等方法对集液器端盖经爆破试验后发生开裂的原因进行了分析,并对原因分析的结果进行了验证。结果表明:端盖犚角处存在拉应力产生渗铜现象以及锡铜合金共化物(IMC)的生成与老化是开裂的主要原因。并提出了预防端盖开裂的措施。
端盖
爆破试验
开裂
拉应力
渗铜
锡铜合金共化物
liquid trap
end shield
blast experiment
cracking
tensile stress
copper leakage
tin-copper alloy
Abstract
Chemical composition analysis, macroscopic and microscopic examination were carried out to analyse the cracking cause of end shield of liquid trap, and the analysis results were verified. The results showed that the tensile stress at R angle region on end shield which led to copper leakage phenomenon and tin-copper alloy (IMC) producing and aging were the main cracking causes after blast experiment. Some measures of preventing end shield from cracking were presented.
中图分类号 TQ051.21
所属栏目
基金项目
收稿日期 2010/6/11
修改稿日期
网络出版日期
作者单位点击查看
备注张敏霞(1972-),女,助理工程师。
引用该论文: ZHANG Min-xia. Analysis on Cracking Cause of End Shield of Liquid Trap after Blast Experiment[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(5): 323～326
张敏霞. 集液器端盖爆破试验后开裂原因分析[J]. 理化检验－物理分册, 2011, 47(5): 323～326
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】廖景娱.金属构件失效分析[M].北京:化学工业出版社,2003:98-99.
【2】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987.
【3】王要利.Sn-2.5Ag-0.7Cu(0.1RE)/Cu焊点界面区微观组织与Cu6Sn5的生长动力学[J].中国有色金属学报,2009,19(4):708-713.
【2】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987.
【3】王要利.Sn-2.5Ag-0.7Cu(0.1RE)/Cu焊点界面区微观组织与Cu6Sn5的生长动力学[J].中国有色金属学报,2009,19(4):708-713.
相关信息