GCr15钢旋压轧辊表面失效原因分析
Surface Failure Reason Analysis on GCr15 Steel Spinning Rollers
摘 要
通过宏观分析、化学成分分析、硬度测试、金相检验、断口分析以及能谱分析等方法对某批GCr15钢旋压轧辊的早期表面崩裂剥落失效原因进行了分析。结果表明: 由于旋压轧辊钢材中的碳化物发生了偏聚, 呈链状和长条状分布, 增加了轧辊的脆性, 降低了轧辊的疲劳寿命, 从而导致轧辊在使用一轮后就在受力最大区域出现了表面崩裂剥落现象, 发生接触疲劳失效。
轧辊
表面崩裂剥落
碳化物偏聚
失效分析
GCr15 steel
roller
surface cleft spalling
carbide gathering
failure analysis
Abstract
By means of macro observation, chemical compositions analysis, hardness testing, metallographic examination, fracture analysis and energy spectrum analysis, early surface cleft spalling failure reason of a batch of GCr15 steel spinning roller was analyzed. The results show that carbide in material of the roller gathered and distributed in formation of chain-type and strip-type, which increased brittleness of the roller and lowered its fatigue life. So surface cleft spalling failure happened at the maximum stress zone only after a round use, and resulted in the contact fatigue failure of the roller.
中图分类号 TG333.17
所属栏目
基金项目
收稿日期 2010/8/8
修改稿日期
网络出版日期
作者单位点击查看
备注乐庸志(1977-),男,工程硕士。
引用该论文: YUE Yong-zhi,QIAN Guo-gang. Surface Failure Reason Analysis on GCr15 Steel Spinning Rollers[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(8): 531～533
乐庸志,钱国钢. GCr15钢旋压轧辊表面失效原因分析[J]. 理化检验－物理分册, 2011, 47(8): 531～533
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵仁高. GCr15钢制轧辊的返新热处理工艺[J]. 山东内燃机, 2001, 12(4): 24-25.
【2】王蕊, 马玥珺, 侯红娟. 轧辊失效原因分析及预防措施[J]. 太原科技大学学报, 2006, 27(9): 85-86.
【3】黄振东. 钢铁金相图谱[M]. 广州: 中国科技文化出版社, 2005:8.
【2】王蕊, 马玥珺, 侯红娟. 轧辊失效原因分析及预防措施[J]. 太原科技大学学报, 2006, 27(9): 85-86.
【3】黄振东. 钢铁金相图谱[M]. 广州: 中国科技文化出版社, 2005:8.
相关信息