汉代铜镜的耐蚀性分析
Analysis on Corrosion Resistance of Bronze Mirror in the Han Dynasty
摘 要
为研究汉代铜镜的耐腐蚀性能, 采用金相检验、扫描电镜和能谱分析、显微硬度测试以及腐蚀试验等分析手段对三面汉代铜镜残片的结构和成分进行了分析。结果表明: 在铜镜表面形成了一层致密的SnO2氧化膜, 能阻止基体铜合金进一步被氧化腐蚀。另外, 铜镜的耐腐蚀性能与古代的热处理技术有关。
氧化膜
腐蚀
成分分析
bronze mirror
oxide film
corrosion
component analysis
Abstract
Metallographic examination, SEM and energy spectrum analysis, microhardness testing and corrosion test were employed to analyze the compositions and structures of three bronze pieces in the Han dynasty to study the corrosion resistance of bronze mirrors in the Han dynasty. The results showed the SnO2 oxidation film on the surface of bronze mirrors could protect copper alloy matrix for further oxidation corrosion. Besides, the corrosion resistance of bronze mirrors was related to the ancient heat treatment technology.
中图分类号 TG17
所属栏目
基金项目
收稿日期 2011/1/11
修改稿日期
网络出版日期
作者单位点击查看
备注牛占蕊(1986-), 女, 硕士研究生。
引用该论文: NIU Zhan-rui,SUN Hong-fei,GUO Na-na,YUAN Bo,WANG Gang. Analysis on Corrosion Resistance of Bronze Mirror in the Han Dynasty[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(9): 550～553
牛占蕊,孙宏飞,郭娜娜,袁博,王刚. 汉代铜镜的耐蚀性分析[J]. 理化检验－物理分册, 2011, 47(9): 550～553
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】贺西林, 李松. 中国古代青铜器艺术[M]. 西安: 陕西人民出版社, 1999.
【2】董亚巍. 中国古代铜镜工艺技术研究[M]. 鄂州: [s.n.],1999.
【3】董亚巍. 从铅含量看古铜镜的铸造月份[C]//全国第七届民间收藏文化高层(湖北 荆州)论坛文集.荆州: [s.n.],2007.
【4】张子高. 从镀锡铜器谈到鋈字本意[J]. 考古学报, 1958(3):73-74.
【5】孙淑云, 周忠福, 韩汝玢, 等.铜镜表面“黑漆古”中“痕像”的研究[J].自然科学史研究,1996,15(2): 179-188.
【6】何堂坤.中国古代铜镜的技术研究[M].北京:紫禁城出版社, 1999:142-170.
【7】张荣军, 张天明. 锡、锌对铜合金耐腐蚀性的影响[J]. 腐蚀与防护, 2007, 28(2):65-69.
【2】董亚巍. 中国古代铜镜工艺技术研究[M]. 鄂州: [s.n.],1999.
【3】董亚巍. 从铅含量看古铜镜的铸造月份[C]//全国第七届民间收藏文化高层(湖北 荆州)论坛文集.荆州: [s.n.],2007.
【4】张子高. 从镀锡铜器谈到鋈字本意[J]. 考古学报, 1958(3):73-74.
【5】孙淑云, 周忠福, 韩汝玢, 等.铜镜表面“黑漆古”中“痕像”的研究[J].自然科学史研究,1996,15(2): 179-188.
【6】何堂坤.中国古代铜镜的技术研究[M].北京:紫禁城出版社, 1999:142-170.
【7】张荣军, 张天明. 锡、锌对铜合金耐腐蚀性的影响[J]. 腐蚀与防护, 2007, 28(2):65-69.
相关信息