大型H型钢气割裂纹原因分析
Reason Analysis of Torch Cutting Cracks on Large H-beam
摘 要
通过宏观检验、硬度测试、化学成分分析、力学性能测试、金相检验及磁记忆应力分析测试等方法对大型H型钢在气割过程中出现裂纹的原因进行了分析。结果表明: 裂纹是由于切割翼板时产生的温差拉应力与材料本身的残余应力相叠加, 作用在应力集中缺口的腹板切割槽处而产生的, 最后对气割和焊接作业过程提出了建议。
气割
裂纹
应力集中
切割方式
温差应力
H-beam
torch cutting
crack
stress concentration
cutting mode
thermal stress
Abstract
The reason of torch cutting cracks on large H-beam was analyzed by means of macrographic examination,hardness testing,chemical composition analysis,mechanical property testing, metallographic examination and magnetic memory testing. The results showed that the crack generated on web incise groove, which was in state of thermal stress and residual stress, and the advices about torch cutting and welding were brought out.
中图分类号 TG142.41 TG487
所属栏目
基金项目
收稿日期 2011/3/16
修改稿日期
网络出版日期
作者单位点击查看
备注王希(1983-), 男, 助理工程师。
引用该论文: WANG Xi,LI Jian-hong,ZHOU Yang,JI Hua-jian. Reason Analysis of Torch Cutting Cracks on Large H-beam[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(9): 586～588
王希,李建宏,周杨,季华建. 大型H型钢气割裂纹原因分析[J]. 理化检验－物理分册, 2011, 47(9): 586～588
被引情况:
【1】陈建芬,陈华锋, "某大型船用曲轴表面裂纹成因分析",理化检验－物理分册 50, 434-437(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘英瑞.莱钢H 型钢的开发研制 [J].钢铁, 2003,38(1):28-30.
【2】徐勇 .莱钢大H型钢生产线工艺技术及设备特点 [J].轧钢, 2009,26(2):36-38.
【3】谢应登, 王伸琨, 李蓓.Q235B热轧 H型钢拉伸试验分层断口的显微分析[J].物理测试, 2004(5):41-43.
【4】郭朝伟. 浅淡H型钢制作容易出现的问题 [J].化工建设工程, 2001(6):29-30.
【2】徐勇 .莱钢大H型钢生产线工艺技术及设备特点 [J].轧钢, 2009,26(2):36-38.
【3】谢应登, 王伸琨, 李蓓.Q235B热轧 H型钢拉伸试验分层断口的显微分析[J].物理测试, 2004(5):41-43.
【4】郭朝伟. 浅淡H型钢制作容易出现的问题 [J].化工建设工程, 2001(6):29-30.
相关信息