给水泵轴横向裂纹分析
Analysis on Transverse Cracks of Water-feeding Pump Shaft
摘 要
某厂生产的给水泵轴在车削加工过程中发现轴中央部位有一条横向裂纹。采用化学成分分析、金相检验和断口分析等方法对裂纹产生的原因进行了分析。结果表明: 该裂纹为锻造裂纹, 锻造温度偏高可能是引起裂纹的重要原因。
横向裂纹
氧化皮
脱碳
锻造裂纹
锻造温度
water-feeding pump shaft
transverse crack
oxide coating
decarburization
forging crack
forging temperature
Abstract
A transverse crack was observed in middle part of water-feeding pump shaft during the turning process. The reason on the crack was analyzed by means of chemical composition analysis, metallographic examination and fracture analysis. The results showed that the transverse crack in water-feeding pump shaft was forging crack, which maybe caused by high forging temperature.
中图分类号 TK414.2+11
所属栏目
基金项目
收稿日期 2010/9/19
修改稿日期
网络出版日期
作者单位点击查看
备注王家敏(1965-), 男, 高级工程师, 学士。
引用该论文: WANG Jia-min,ZENG Zhen-peng,HE Ping. Analysis on Transverse Cracks of Water-feeding Pump Shaft[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(9): 591～593
王家敏,曾振鹏,何平. 给水泵轴横向裂纹分析[J]. 理化检验－物理分册, 2011, 47(9): 591～593
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吕炎.锻造组织性能控制[M].北京:国防工业出版社,1988:226.
【2】《锻件质量分析》编写组.锻件质量分析[M].北京:机械工业出版社,1983:22.
【3】孙盛玉.热处理裂纹分析图谱[M].大连: 大连出版社,2003: 14.
【4】《大型铸锻件缺陷分析图谱》编委会.大型铸锻件缺陷分析图谱[M].北京: 机械工业出版社,1990:2-4,131-139.
【2】《锻件质量分析》编写组.锻件质量分析[M].北京:机械工业出版社,1983:22.
【3】孙盛玉.热处理裂纹分析图谱[M].大连: 大连出版社,2003: 14.
【4】《大型铸锻件缺陷分析图谱》编委会.大型铸锻件缺陷分析图谱[M].北京: 机械工业出版社,1990:2-4,131-139.
相关信息