40CrNiMoA钢螺栓断裂原因分析
Fracture Cause Analysis of 40CrNiMoA Steel Bolts
摘 要
通过宏观检验、断口分析、金相检验、硬度测试及化学成分分析等方法对40CrNiMoA钢螺栓断裂的原因进行了分析。结果表明: 螺栓的断裂性质为氢脆断裂, 产生原因是螺栓制造过程中残留的氢含量过高所致。
螺栓
氢脆断裂
40CrNiMoA steel
bolt
hydrogen brittleness fracture
Abstract
Fracture cause of 40CrNiMoA steel bolts was analyzed by means of macroscopic examination, fracture analysis, metallographic examination, hardness testing and chemical composition analysis. The results showed that the fracture mechanism was the hydrogen brittleness fracture, the reason of fracture was due to high absorption content of hydrogen during producing process of the bolts.
中图分类号 TK418
所属栏目
基金项目
收稿日期 2010/11/29
修改稿日期
网络出版日期
作者单位点击查看
备注陈昌达(1975-), 男, 工程师。
引用该论文: CHEN Chang-da. Fracture Cause Analysis of 40CrNiMoA Steel Bolts[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(9): 602～604
陈昌达. 40CrNiMoA钢螺栓断裂原因分析[J]. 理化检验－物理分册, 2011, 47(9): 602～604
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陶春虎, 钟培道, 恩云飞,等.军工产品失效分析技术手册[M].北京: 国防工业出版社, 2009.
【2】刘昌奎, 臧金鑫, 张兵.30CrMnSiA螺栓断裂原因分析[J].失效分析与预防, 2008,3(2):42-47.
【3】张栋, 钟培道, 陶春虎,等.失效分析[M].北京: 国防工业出版社, 2004.
【4】张家付, 王维, 冯抗屯.40CrNi2Si2MoVA钢螺桩断裂分析[J].失效分析与预防, 2008,3(4):51-54.
【2】刘昌奎, 臧金鑫, 张兵.30CrMnSiA螺栓断裂原因分析[J].失效分析与预防, 2008,3(2):42-47.
【3】张栋, 钟培道, 陶春虎,等.失效分析[M].北京: 国防工业出版社, 2004.
【4】张家付, 王维, 冯抗屯.40CrNi2Si2MoVA钢螺桩断裂分析[J].失效分析与预防, 2008,3(4):51-54.
相关信息