电力机车电机转轴组件断裂分析
Fracture Analysis of Electric Engine Rotating Shaft Subassembly of Electric Locomotive
摘 要
通过宏观及微观分析方法对电机转轴组件发生非正常早期断裂的原因进行了分析。结果表明: 在腐蚀环境及循环应力的共同作用下, 电机转轴组件产生局部腐蚀开裂及疲劳扩展, 导致了组件的最终失效, 属腐蚀疲劳断裂, 且电机转轴先于其内套小齿轮轴发生断裂。
齿轮轴
腐蚀疲劳
晶间腐蚀
腐蚀坑
应力集中
electric engine rotating shaft
pinion shaft
corrosion fatigue
intergranular corrosion
etch pit
stress concentration
Abstract
Rotating shaft subassembly of electric locomotive happened to fracture abnormally at early stage. The fracture reason was researched by means of macroscopical and microscopical analysis. The results showed that localized corrosion cracking and fatigue expansion occurred in rotating shaft subassembly under the combined action of erosive environment and cyclic stress. The fracture of rotating shaft subassembly was corrosion fatigue fracture, and rotating shaft was ruptured earlier than that in the interior pinion shaft.
中图分类号 TG111.8 U260.332
所属栏目
基金项目
收稿日期 2011/2/24
修改稿日期
网络出版日期
作者单位点击查看
备注张彦文(1972-),男, 高级工程师, 博士研究生。
引用该论文: ZHANG Yan-wen,WU Li-xin,ZHANG You-deng,WANG Yue. Fracture Analysis of Electric Engine Rotating Shaft Subassembly of Electric Locomotive[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(11): 729～733
张彦文,吴立新,张友登,王悦. 电力机车电机转轴组件断裂分析[J]. 理化检验－物理分册, 2011, 47(11): 729～733
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】项彬, 刘鑫贵, 何忠, 等.铁路货车车轴断裂分析[J].理化检验-物理分册,2004,40(9):461-464.
【2】廖景娱.金属构件失效分析[M].北京: 化学工业出版社, 2003:81.
【3】孙智, 江利, 应鹏展.失效分析——基础与应用[M].北京: 机械工业出版社, 2005:158-160.
【4】梁思祖, 杨金山, 梁耀能,等.柴油机进气门断裂原因分析[J].理化检验-物理分册,2005,41(z1):208.
【2】廖景娱.金属构件失效分析[M].北京: 化学工业出版社, 2003:81.
【3】孙智, 江利, 应鹏展.失效分析——基础与应用[M].北京: 机械工业出版社, 2005:158-160.
【4】梁思祖, 杨金山, 梁耀能,等.柴油机进气门断裂原因分析[J].理化检验-物理分册,2005,41(z1):208.
相关信息