16MnD5钢板焊接件热影响区开裂原因分析
Cause Analysis on Heat Affected Zone Cracking of Weldments of 16MnD5 Steel
摘 要
采用化学成分分析、低倍检验、金相检验、显微硬度测试等方法对16MnD5低合金高强度钢板焊接件热影响区开裂的原因进行了分析。结果表明: 裂纹起始于热影响区粗晶区, 裂纹以沿晶和穿晶混合方式扩展, 为以残余应力和母材淬硬倾向为主因的冷裂纹。
焊接热影响区
冷裂纹
残余应力
淬硬倾向
16MnD5 steel plate weldment
heat affected zone
cold crack
residual stress
tendentiousness of harden quenching
Abstract
Cause analysis was conducted on the heat affected zone (HAZ) cracking of a high strength low alloy 16MnD5 steel plate weldment by the methods of chemical compositions analysis, macroscopic examination, metallographic examination and microhardness test. The results show that the crack began from the coarse grain zone of the HAZ, and extended in the mixed manner of intergranular and transgranular. The crack was cold crack which was mainly caused by residual stress and the base metal’s tendentiousness of harden quenching.
中图分类号 TG457.11
所属栏目
基金项目
收稿日期 2011/9/22
修改稿日期
网络出版日期
作者单位点击查看
备注王新娟(1981-),女,助理工程师,学士。
引用该论文: WANG Xin-juan,WANG Ying,XIA Cong-xin. Cause Analysis on Heat Affected Zone Cracking of Weldments of 16MnD5 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(12): 796～798
王新娟,王莹,夏从鑫. 16MnD5钢板焊接件热影响区开裂原因分析[J]. 理化检验－物理分册, 2011, 47(12): 796～798
被引情况:
【1】石宁,李晨, "40CrNiMoA钢轮缘堆焊层裂纹产生原因分析",理化检验－物理分册 52, 202-205(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】史耀武. 中国材料工程大典 第22卷 材料焊接工程(上)[M]. 北京:化学工业出版社,2006: 164-165.
【2】中国机械工程学会焊接学会. 焊接手册 第2卷 材料的焊接[M]. 北京:机械工业出版社,2008:138,266.
【3】第一机械工业部哈尔滨焊接研究所. 焊接裂缝金相分析图谱[M]. 哈尔滨:黑龙江科学技术出版社,1981: 49-52.
【4】杨松. 锅炉压力容器焊接技术培训教材[M]. 北京:机械工业出版社,2005: 70-71,165.
【5】李亚江,刘强,王娟,等. 焊接质量控制与检验[M]. 北京:化学工业出版社,2006: 45.
【2】中国机械工程学会焊接学会. 焊接手册 第2卷 材料的焊接[M]. 北京:机械工业出版社,2008:138,266.
【3】第一机械工业部哈尔滨焊接研究所. 焊接裂缝金相分析图谱[M]. 哈尔滨:黑龙江科学技术出版社,1981: 49-52.
【4】杨松. 锅炉压力容器焊接技术培训教材[M]. 北京:机械工业出版社,2005: 70-71,165.
【5】李亚江,刘强,王娟,等. 焊接质量控制与检验[M]. 北京:化学工业出版社,2006: 45.
相关信息