吊车转盘连接螺栓断裂分析
Fracture Analysis on Binding Bolt of Crane Turnplate
摘 要
吊车转盘后部的连接螺栓发生断裂, 通过化学成分分析、宏观和微观检验等方法对断裂原因进行了分析。结果表明: 螺栓为疲劳断裂, 螺纹根部的细小裂纹是导致螺栓发生疲劳断裂的主要原因; 螺栓松动后受到弯曲载荷是引起螺栓发生疲劳断裂的诱因。
高强度螺栓
疲劳断裂
表面缺陷
松动
crane turnplate
high strength bolt
fatigue fracture
surface defect
loose
Abstract
Binding bolts of the crane turnplate were fractured. By means of chemical composition analysis, macro and micro examination, the fracture reason was analyzed. The results showed that the fracture reason of bolt was found as fatigue fracture.The fatigue fracture was mainly caused by the defects in root of screw.After bolt loosening, the fracture was caused by the fatigue failure under the bending loads.
中图分类号 TG142.41
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/7/27
修改稿日期
网络出版日期
作者单位点击查看
备注余其中(1978-), 男, 工程师, 学士。
引用该论文: YU Qi-zhong. Fracture Analysis on Binding Bolt of Crane Turnplate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(3): 194～196
余其中. 吊车转盘连接螺栓断裂分析[J]. 理化检验－物理分册, 2012, 48(3): 194～196
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】崔约贤, 王长利. 金属断口分析[M]. 哈尔滨:哈尔滨工业大学出版社,1998:77-78.
【2】陈龙, 张慧, 邱明, 等.转盘轴承螺栓连接特性分析[J]. 轴承,2009(8): 10-13.
【3】钟玉柱, 张为波, 宋祥献.挖掘机回转支承螺栓断裂诊断与预防[J]. 建筑机械,2009(7): 97-100.
【2】陈龙, 张慧, 邱明, 等.转盘轴承螺栓连接特性分析[J]. 轴承,2009(8): 10-13.
【3】钟玉柱, 张为波, 宋祥献.挖掘机回转支承螺栓断裂诊断与预防[J]. 建筑机械,2009(7): 97-100.
相关信息