316L不锈钢人孔盖板爆裂原因分析
Reason Analysis on Bursting of Manhole Cover of 316L Stainless Steel
摘 要
通过化学成分分析、宏观与微观检验、腐蚀产物分析等方法, 对316L不锈钢人孔盖板发生爆裂的原因进行了分析。结果表明: 人孔盖板爆裂是由应力腐蚀引起的。造成应力腐蚀的原因是采用冷冲压成型的球形人孔盖板具有较大的残余拉应力, 而其工作环境中也存在周期性变化的工作应力。
人孔盖板
应力腐蚀
真空制盐
stainless steel
manhole cover
stress corrosion
vacuum salt production
Abstract
The bursting reason of manhole cover of 316L stainless steel was analyzed by means of chemical composition analysis, macro and micro examination, corrosion product analysis. The results showed that manhole cover bursted due to stress corrosion. The reason of stress corrosion was that there would be strong residual stress in hemispherical manhole cover by cold pressing, while stress with cyclical change also existed in the working condition.
中图分类号 TG142.71
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/6/28
修改稿日期
网络出版日期
作者单位点击查看
备注刘劲松(1986-), 男, 助理工程师。
引用该论文: LIU Jin-song,CHANG Zhi-ping,WU Jin-qiang. Reason Analysis on Bursting of Manhole Cover of 316L Stainless Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(3): 197～199
刘劲松,常治平,吴进强. 316L不锈钢人孔盖板爆裂原因分析[J]. 理化检验－物理分册, 2012, 48(3): 197～199
被引情况:
【1】黎华,王恋,林金梅, "高温高压染色机壳体破裂分析",理化检验－物理分册 50, 512-514(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陆世英,张廷凯,康喜范,等.不锈钢[M]. 北京:原子能出版社,1995:246.
【2】张栋,钟培道.失效分析[M]. 北京:国防工业出版社,2008:194-197.
【3】REVIE R W.尤利格腐蚀手册[M]. 杨武,译.北京:化学工业出版社,2005:138-141.
【4】吴剑.不锈钢的腐蚀破坏与防蚀技术[J]. 腐蚀与防护,1997,18(4):38-40.
【5】骆素珍,彭建国.316L不锈钢换热器的失效原因分析[J]. 宝钢技术,2007(4):24-28.
【6】龚敏,余祖孝,陈琳.金属腐蚀理论及腐蚀控制[M]. 北京:化学工业出版社,2009:121.
【2】张栋,钟培道.失效分析[M]. 北京:国防工业出版社,2008:194-197.
【3】REVIE R W.尤利格腐蚀手册[M]. 杨武,译.北京:化学工业出版社,2005:138-141.
【4】吴剑.不锈钢的腐蚀破坏与防蚀技术[J]. 腐蚀与防护,1997,18(4):38-40.
【5】骆素珍,彭建国.316L不锈钢换热器的失效原因分析[J]. 宝钢技术,2007(4):24-28.
【6】龚敏,余祖孝,陈琳.金属腐蚀理论及腐蚀控制[M]. 北京:化学工业出版社,2009:121.
相关信息