Torch Brazing Methods for Cast Iron QT500-7 and Its Influence on Performance of Brazed Joints
摘 要
以B-Ag40CuZnCdNi合金为钎料, 采用火焰钎焊方法实现了QT500-7铸铁的连接。研究了“三明治”法和毛细法两种钎料放置方式及不同加热时间对钎焊接头抗剪强度的影响, 并对连接界面的微观组织进行了分析。结果表明: 用“三明治”法放置钎料时, 接头容易产生焊接缺陷, 接头的承载能力低于母材; 用毛细法放置钎料时, 在足够长的加热时间条件下, 液态钎料的填缝过程同时具有清洁钎缝间隙的作用, 有利于得到钎缝细小平直且缺陷少的接头, 因此抗剪强度得到提高, 加热时间大于5 min时, 接头承载能力高于母材, 但加热时间不足时反而不如“三明治”法的施焊效果。
Abstract
Using B-Ag40CuZnCdNi alloy as filler metal, cast iron QT500-7 was connected by torch brazing. The effect of filler metal placement method and heating time on the shear strength of the brazed joints was studied by shear test and microstructure observation. The results showed that when sandwich method was used to place the filler metal, the joint was likely to cause welding defects, and the carrying capacity of the joint was lower than that of base metal. When capillary method was used in enough heating time, the filling process of the liquid metal had also played a role of cleaning the gap of brazing seam, which was helpful to get the joint with thin and straight brazing seam and less defects, so the shear strength had been improved, when the heating time was more than 5 min, the carrying capacity of the joint was higher than that of base metal, but it will be not as good as sandwich method if the heating time was insufficient.
中图分类号 TG454
所属栏目 试验技术与方法
基金项目
收稿日期 2011/10/10
修改稿日期
网络出版日期
作者单位点击查看
备注王振波(1986-), 男, 硕士。
引用该论文: WANG Zhen-bo,CHEN Chun-huan. Torch Brazing Methods for Cast Iron QT500-7 and Its Influence on Performance of Brazed Joints[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(5): 306~309
王振波,陈春焕. QT500-7铸铁火焰钎焊方法及其对接头性能的影响[J]. 理化检验-物理分册, 2012, 48(5): 306~309
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】彭高峨.球墨铸铁焊接和焊接材料的国内外现状[J].焊接,1987(1):9-12.
【2】中国机械工程学会焊接分会.焊接手册[M].3版.北京: 机械工业出版社,2008.
【3】中国电子科技集团电科院电子电路柔性制造中心. SMT连接技术手册[M].北京: 电子工业出版社,2008.
【4】ZHOU X B, DE HOSSON JTHM. Reactive wetting of liquid metals on ceramic substrates[J].ActaMaterialia,1996,44(2):421-426.
【5】薛松柏,董健,吕晓春.Al/Cu管异种材料火焰钎焊连接[J].焊接,2003(12):23-25.
【6】孙荣禄,李慕勤,张九海,等.中间过渡金属对钛合金和不锈钢扩散焊接头强度的影响[J].焊接学报,1996,17(4):212-218.
【2】中国机械工程学会焊接分会.焊接手册[M].3版.北京: 机械工业出版社,2008.
【3】中国电子科技集团电科院电子电路柔性制造中心. SMT连接技术手册[M].北京: 电子工业出版社,2008.
【4】ZHOU X B, DE HOSSON JTHM. Reactive wetting of liquid metals on ceramic substrates[J].ActaMaterialia,1996,44(2):421-426.
【5】薛松柏,董健,吕晓春.Al/Cu管异种材料火焰钎焊连接[J].焊接,2003(12):23-25.
【6】孙荣禄,李慕勤,张九海,等.中间过渡金属对钛合金和不锈钢扩散焊接头强度的影响[J].焊接学报,1996,17(4):212-218.
相关信息