TC11钛合金棒开裂原因分析
Analysis on Cracking Reason of TC11 Titanium Bar
摘 要
TC11合金钛棒在退火后发现裂纹。为分析裂纹产生的原因, 对其进行了裂纹宏观和微观检验、显微硬度测试和能谱分析。结果表明: 原材料在冶炼过程中氧、碳含量偏高聚集在材料中形成偏析, 在轧制过程中开裂, 退火后发现的钛棒纵表面的裂纹是由原材料带来的。
裂纹
显微硬度
偏析
TC11 titanium bar
crack
microhardness
segregation
Abstract
The cracks in TC11 titanium bar were detected after annealing. In order to find out the cracking reason, macro and micro morphology, microhardness and energy spectrum of the bar were analyzed. The results showed that high content oxygen and carbon gathered in raw materials form in segregation, the bar was cracked in rolling. The cracks found on longitudinal surface of titanium bar after annealing were brought from raw materials.
中图分类号 TG146.2+3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/7/27
修改稿日期
网络出版日期
作者单位点击查看
备注吴俊峰(1977-), 男, 工程师, 工学学士。
引用该论文: WU Jun-feng. Analysis on Cracking Reason of TC11 Titanium Bar[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(5): 331～333
吴俊峰. TC11钛合金棒开裂原因分析[J]. 理化检验－物理分册, 2012, 48(5): 331～333
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张卫方, 刘庆瑔, 陶春虎, 等.钛合金损伤与预防的研究进展[J].材料工程,2003(z1):20-24.
【2】陶春虎,曹春晓,张卫方,等.航空用钛合金的失效及其预防[M].北京:国防工业出版社,2002.
【3】航空物理冶金培训教材编审组.金相检验技术[M].北京:[s.n.],1997.
【2】陶春虎,曹春晓,张卫方,等.航空用钛合金的失效及其预防[M].北京:国防工业出版社,2002.
【3】航空物理冶金培训教材编审组.金相检验技术[M].北京:[s.n.],1997.
相关信息