齿轮箱轴断裂分析
Fracture Analysis of Shaft in Gear Box
摘 要
采用化学成分分析、断口分析、金相检验和力学性能测试, 对某齿轮箱轴发生断裂的原因进行了分析。结果表明: 其断裂模式为疲劳断裂, 起源于退刀槽尖角位置, 直角退刀槽造成应力集中产生疲劳裂纹; 而原材料的锻造和热处理工艺不合理, 加速了轴的疲劳断裂。
疲劳断裂
退刀槽
热处理
shaft in gear box
fatigue fracture
tool withdrawal chute
heat treatment
Abstract
The fracture reason of the shaft in gear box was analyzed by means of chemical composition analysis, fracture analysis, metallographic examination and mechanical properties testing. The results showed that the fatigue fracture mode was determined, which originated from the sharp angle of the tool withdrawal chute. The right-angle withdrawal chute caused stress concentration. The unreasonable forging and heat-treatment process of material accelerated the fatigue fracture of the shaft.
中图分类号 TH133.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/5/11
修改稿日期
网络出版日期
作者单位点击查看
备注陈刚(1970-), 男, 工程师, 硕士。
引用该论文: CHEN Gang. Fracture Analysis of Shaft in Gear Box[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(5): 334～336
陈刚. 齿轮箱轴断裂分析[J]. 理化检验－物理分册, 2012, 48(5): 334～336
被引情况:
【1】杨星红,王荣, "电梯驱动轴断裂原因分析",理化检验－物理分册 50, 292-295(2014)
【2】谢金鹏,钟振前,冯冉, "某压缩机45钢转轴断裂原因分析",理化检验－物理分册 50, 919-921(2014)
【3】樊伟刚,张辉,牛红莲,张亚梅,潘彦国, "9Cr18MoV钢丝杠耳轴断裂失效分析",理化检验－物理分册 50, 603-605(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】DAVIS H E, TROXELL G E, HAUCK G F W. The Testing of Engineering Materials[M].New York:McGraw-Hill Book Company,1982:256.
【2】毛晓禹.断口学译文集[M].包头: 《兵器材料与力学》编辑部, 1980.
【3】董毅.减速机轴断裂分析[J].理化检验-物理分册,2003,39(10): 538-540.
【4】陈玲琳, 朱邵峰. 旋回破碎机主轴断裂分析[J].金属热处理,2006,31(6):87-88.
【2】毛晓禹.断口学译文集[M].包头: 《兵器材料与力学》编辑部, 1980.
【3】董毅.减速机轴断裂分析[J].理化检验-物理分册,2003,39(10): 538-540.
【4】陈玲琳, 朱邵峰. 旋回破碎机主轴断裂分析[J].金属热处理,2006,31(6):87-88.
相关信息