0Cr25Ni22Mn5Mo2堆焊层超低含量δ-铁素体的测定
Determination of Super-low δ-Ferrite Content of 0Cr25Ni22Mn5Mo2 Surfacing Layer
摘 要
采用0Cr25Ni22Mn5Mo2合金焊丝在16MnR低合金钢表面堆焊形成堆焊层, 采用光学显微镜、扫描电镜和电子背散射衍射仪等仪器对堆焊层的相组成及含量进行了分析。结果表明: 0Cr25Ni22Mn5Mo2堆焊层的显微组织主要为奥氏体, δ-铁素体含量极少, 电子背散射衍射技术可以用作堆焊层中细小物相的分析, 并获得极低含量的物相数; 电子背散射衍射技术在焊接材料的分析中具有广阔的应用前景。
堆焊层
δ-铁素体含量
电子背散射衍射
0Cr25Ni22Mn5Mo2 alloy
surfacing layer
δ-ferrite content
EBSD
Abstract
Surfacing layer was welded on 16MnR low-alloy steel surface with 0Cr25Ni22Mo2 alloy electrode, and the phase compositions and content were analyzed by optical microscope, scanning electronic microscope and electron back scattering diffraction (EBSD). It results show that microstructure of 0Cr25Ni22Mo2 surfacing layer mainly consisted of austenite and very little δ-ferrite. It was conformed that EBSD technique can be used to analyze the tiny phase and obtain it super-low content, which is beneficial for analysis on the welding material.
中图分类号 TG455
所属栏目 试验技术与方法
基金项目
收稿日期 2011/10/26
修改稿日期
网络出版日期
作者单位点击查看
备注万友娟(1975-),女,工程师。
引用该论文: WAN You-juan,YANG Xiao-min,CHEN Fang-yu. Determination of Super-low δ-Ferrite Content of 0Cr25Ni22Mn5Mo2 Surfacing Layer[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(8): 516～518
万友娟,杨小敏,陈方玉. 0Cr25Ni22Mn5Mo2堆焊层超低含量δ-铁素体的测定[J]. 理化检验－物理分册, 2012, 48(8): 516～518
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李亚江,魏星. 奥氏体不锈钢焊缝中的δ-铁素体特征[J]. 焊接研究与生产,1996(4):2-4.
【2】何德孚, 蔡新强, 徐阿敏,等. 奥氏体不锈钢焊管焊缝铁素体含量及其测定[J]. 焊管,2007,30(5):30-35.
【3】王仁卉, 桂嘉年, 陈小梅, 等. 电子背散射衍射在取向测定和相分析中的应用[J]. 电子显微学报, 1998(5): 45-47.
【2】何德孚, 蔡新强, 徐阿敏,等. 奥氏体不锈钢焊管焊缝铁素体含量及其测定[J]. 焊管,2007,30(5):30-35.
【3】王仁卉, 桂嘉年, 陈小梅, 等. 电子背散射衍射在取向测定和相分析中的应用[J]. 电子显微学报, 1998(5): 45-47.
相关信息