680t/h电站锅炉高温过热器爆管原因分析及预防措施
Cause Analysis and Preventive Measures on Bursting of High Temperature Superheater Tubes of 680t/h Power Station Boiler
摘 要
某台680t/h电站锅炉高温过热器最近发生两起爆管事故, 通过对爆管样管进行宏观检验、化学成分分析和金相检验判断爆管的根本原因。结果表明: 由于长时间超温运行导致管子早期蠕变引起爆管, 并采取了有效的预防措施。
爆管
超温
早期燸变
措施
high temperature superheater
burst tube
overheating
prevention measure
Abstract
Bursting of high temperature superheater tubes of 680t/h power station boiler coccured twice re-cently, and macroscopic examination, chemical compositions analysis and metallographic examination were investiga-ted to find the casuse, the results showed that the failure was due to overheat which led to primary creep, then someeffective prevention was taken.
中图分类号 TK223.3+2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/12/27
修改稿日期
网络出版日期
作者单位点击查看
备注王小聪(1982-), 男, 工程师, 工学硕士。
引用该论文: WANG Xiao-cong,LI Hua,MA Kuo,LU Zhong-ming. Cause Analysis and Preventive Measures on Bursting of High Temperature Superheater Tubes of 680t/h Power Station Boiler[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(11): 770～772
王小聪,黎华,马括,卢忠铭. 680t/h电站锅炉高温过热器爆管原因分析及预防措施[J]. 理化检验－物理分册, 2012, 48(11): 770～772
被引情况:
【1】缪春辉,汤 泉,张 涛,陈国宏, "某火力发电厂水冷蒸发屏管泄漏原因分析及处理",理化检验－物理分册 52, 574-577(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴磊, 顾昌.1 025t/h锅炉高温过热器爆管原因分析[J].湖北电力, 2004, 28(1): 23-26.
【2】王仁志.1 025t/h锅炉末级过热器爆管原因分析[J].华东电力, 2000(11): 35-36.
【3】张建国, 孔祥瑜.电站锅炉屏式过热器爆管分析[J].能源研究与利用, 1999(5): 34-36.
【4】王莹, 吴少华, 秦裕琨, 等.大型电站锅炉过热器爆管原因综述及对策[J].中国电力, 1998, 31(10): 26-29.
【5】周昊, 池作和, 李凤瑞, 等.根据爆口特征判断爆管原因[J].热力发电, 1995(5): 43-48.
【2】王仁志.1 025t/h锅炉末级过热器爆管原因分析[J].华东电力, 2000(11): 35-36.
【3】张建国, 孔祥瑜.电站锅炉屏式过热器爆管分析[J].能源研究与利用, 1999(5): 34-36.
【4】王莹, 吴少华, 秦裕琨, 等.大型电站锅炉过热器爆管原因综述及对策[J].中国电力, 1998, 31(10): 26-29.
【5】周昊, 池作和, 李凤瑞, 等.根据爆口特征判断爆管原因[J].热力发电, 1995(5): 43-48.
相关信息