曲面齿根X射线应力测试
X-ray Stress Measurement of Gear Root Curved Surface
摘 要
采用X射线衍射法测试了小曲率齿根表面的切向残余应力, 研究了通过限制X射线照射宽度降低曲面衍射效应的方法。结果表明: 当照射宽度小于1/3齿根曲率半径时, 可忽略曲面衍射效应的不利影响, 确保X射线应力测试结果的可靠性。
X射线应力测试
照射宽度
gear root curved surface
X-ray residual stress measurement
irradiation width
Abstract
X-ray stress analysis method was used to measure the tangential residual stress of small curvature gear root surface, and the X-ray irradiation width was confined to overcome the curve diffraction effect. The results show that when the irradiation width was less than one third of the curve radius, the curve diffraction effect could be ignored and the residual stress measurement results are reliable.
中图分类号 TG115.22+1
所属栏目 试验与研究
基金项目
收稿日期 2012/3/19
修改稿日期
网络出版日期
作者单位点击查看
备注唐亮(1983-),男,工程师,硕士。
引用该论文: TANG Liang,DAI Ru-yong,LIU Zhong-wei,ZHAN Ke,JIANG Chuan-hai. X-ray Stress Measurement of Gear Root Curved Surface[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(4): 223～224
唐亮,戴如勇,刘忠伟,詹科,姜传海. 曲面齿根X射线应力测试[J]. 理化检验－物理分册, 2013, 49(4): 223～224
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】米谷茂. 残余应力的产生和对策[M]. 北京: 机械工业出版社,1983.
【2】朱晨,姜传海. 17Cr2Ni2Mo的表面复合喷丸强化[J]. 机械工程材料, 2011,35(9): 98-99.
【3】栾卫志, 姜传海, 嵇宁. 09-TiB26351Al复合材料喷丸层再结晶过程的X射线衍射分析[J]. 金属学报, 2008,44(9): 671-674.
【4】张定铨,何家文. 材料中残余应力的X射线衍射分析和作用[M]. 西安: 西安交通大学出版社,1999.
【2】朱晨,姜传海. 17Cr2Ni2Mo的表面复合喷丸强化[J]. 机械工程材料, 2011,35(9): 98-99.
【3】栾卫志, 姜传海, 嵇宁. 09-TiB26351Al复合材料喷丸层再结晶过程的X射线衍射分析[J]. 金属学报, 2008,44(9): 671-674.
【4】张定铨,何家文. 材料中残余应力的X射线衍射分析和作用[M]. 西安: 西安交通大学出版社,1999.
相关信息