压缩机电动阀阀杆断裂原因分析
Reasons Analysis on Fracture of a Compressor Electric Valve Stem
摘 要
从断口宏观特征、化学成分、显微组织以及硬度等方面对某电动阀阀杆的断裂原因进行了分析。结果表明: 由于断裂阀杆材料韧性不足, 局部存在网状和带状碳化物, 严重降低了材料的断裂抗力,是导致阀杆脆性断裂的主要原因; 位于阀杆上端面内螺纹根部的断裂源存在机加工缺口, 造成局部应力集中, 导致阀杆在缺口处起裂。
碳化物
韧性不足
脆性断裂
valve stem
carbide
toughness shortage
brittle fracture
Abstract
The fracture reasons of a compressor electric valve stem were analyzed by means of macroscopical frature analysis, chemical compositions analysis, metallographic structure analysis and hardness test. The results show that the poor toughness of the fractured valve stem material and the local existence of network and banded carbides seriously lowered the fracture resistance of the material, which was the main cause of brittle fracture of the valve stem. The fracture position existing machining gap that located in the interior thread roots of upper extreme of the fracture valve stem caused local stress concentration and led the valve stem to crack from the gap.
中图分类号 TG115
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/7/22
修改稿日期
网络出版日期
作者单位点击查看
备注王勇(1970-),男,工程师。
引用该论文: WANG Yong,JI Hua-jian,WEN Jia-hui,CHEN Hai. Reasons Analysis on Fracture of a Compressor Electric Valve Stem[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(4): 263～265
王勇,季华建,文佳卉,陈海. 压缩机电动阀阀杆断裂原因分析[J]. 理化检验－物理分册, 2013, 49(4): 263～265
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李炯辉, 林德成. 金属材料金相图谱[M]. 北京: 机械工业出版社, 2006.
【2】胡世炎. 破断故障金相分析[M]. 北京: 国防工业出版社, 1979.
【3】美国金属学会. 金属手册[M]. 北京: 机械工业出版社, 1985.
【4】谭毅. 石化装置寿命预测与失效分析工程实例[M]. 北京: 化学工业出版社, 2007.
【5】吴连生. 失效分析及其应用[J]. 理化检验-物理分册,1995,31(4): 56-59.
【2】胡世炎. 破断故障金相分析[M]. 北京: 国防工业出版社, 1979.
【3】美国金属学会. 金属手册[M]. 北京: 机械工业出版社, 1985.
【4】谭毅. 石化装置寿命预测与失效分析工程实例[M]. 北京: 化学工业出版社, 2007.
【5】吴连生. 失效分析及其应用[J]. 理化检验-物理分册,1995,31(4): 56-59.
相关信息