塔里木油田非API油、套管失效分析及预防
Failure Analysis and Prevention of Non-API Tubing and Casing in Tarim Oil Field
摘 要
对塔里木油田非API油、套管的失效情况进行了统计分析, 总结了油、套管常见的失效形式及失效原因, 并针对每种失效形式提出了一定的预防措施。结果表明: 套管压力升高主要是因油管接头泄漏所致, 而油管接头泄漏主要是因为其气密封性能不能满足油田实际工况条件, 套管挤毁失效主要与套管磨损地层蠕变有关, 套管断裂和开裂既与套管材质有关, 也与套管磨损有关; 通过制定严格的油、套管订货技术标准, 可有效预防和减少塔里木油田非API油、套管失效事故的发生。
油管
套管
特殊螺纹接头
泄漏
挤毁
断裂
Tarim oil field
tubing
casing
premium connection
leakage
collapse
fracture
Abstract
Statistic analysis of the failure cases of non-API tubing and casing in Tarim oil field was done and normal failure form and cause were summarized, and some prevention measures were put forward. The results show that the cause of tubing joint leakage was its bad gas seal capability being lower than the actual use condition that results in the casing pressure increase, the casing collapse was due to casing worn and stratum creep, and the casing fracture and crack was not only related to casing material quality, but also related to casing worn. Tubing and casing should be prevented from failure by establishing some tubing and casing technical specification for buy.
中图分类号 TE92
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/4/24
修改稿日期
网络出版日期
作者单位点击查看
备注刘建勋(1963-),男,教授级高级工程师。
引用该论文: LIU Jian-xun,LV Shuan-lu,GAO Yun-zong,YANG Xiang-tong,ZHU Jin-zhi,PENG Jian-yun,BAI Xiao-fei,RAO Wen-yi. Failure Analysis and Prevention of Non-API Tubing and Casing in Tarim Oil Field[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(6): 416～418
刘建勋,吕拴录,高运宗,杨相同,朱金智,彭建云,白晓飞,饶文艺. 塔里木油田非API油、套管失效分析及预防[J]. 理化检验－物理分册, 2013, 49(6): 416～418
被引情况:
【1】谢俊峰,宋文文,常泽亮,吕拴录,文志明,吴云才,秦德友, "某天然气井13Cr油管腐蚀原因",腐蚀与防护 35, 754-757(2014)
【2】吕拴录,彭建新,王鹏,宋文文,宋生印,王新虎,李金凤,耿海龙,徐永康, "某井油管穿孔原因分析",理化检验－物理分册 51, 508-511(2015)
【3】吕拴录,杨向同,宋文文,董仁,王新虎,王鹏,李金凤,饶文艺,耿海龙, "某井超级13Cr钢特殊螺纹接头油管接箍横向开裂原因分析",理化检验－物理分册 51, 297-301(2015)
【4】张玉福,宋文明,马颖,郝远,卢雪梅, "空冷器翅片管泄漏原因分析",理化检验－物理分册 51, 488-492(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吕拴录, 骆发前, 陈飞, 等. 牙哈7X-1井套管压力升高原因分析[J]. 钻采工艺, 2008, 31(1): 129-132.
【2】吕拴录, 王震, 康延军, 等. 某气井完井管柱泄漏原因分析[J]. 油气井测试, 2010, 19(4): 58-60.
【3】张福祥,吕拴录,王振彪, 等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全, 2010,26(5): 65-68.
【4】吕拴录, 李元斌, 王振彪, 等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J]. 腐蚀与防护, 2010, 31(11): 902-904.
【5】LV Shuan-lu, LI Zhi-hou,HAN Yong. High dogleg severity,wear ruptures casing string[J]. Oil & Gas, 2004, 98(49): 74-80.
【6】许峰, 吕拴录, 康延军, 等. 井口套管磨损失效原因分析及预防措施研究[J]. 石油钻采工艺, 2011, 33(2): 140-142.
【7】LV Shuan-lu, TENG Xue-qing, KANG Yan-jun,et al. Analysis on causes of a well casing coupling crack[J]. Materials Performance, 2012,51(4):58-62.
【8】吕拴录, 李鹤林. V150套管接箍破裂原因分析[J]. 理化检验-物理分册,2005, 41(增1): 285-290.
【9】吕拴录, 张福祥, 李元斌, 等. 塔里木油气田非API油井管使用情况统计分析[J]. 石油矿场机械, 2009,38(7): 70-74.
【10】吕拴录, 韩勇. 特殊螺纹接头油、套管使用及展望[J]. 石油工业技术监督,2003(3):1-4.
【11】吕拴录. 特殊螺纹接头油套管选用注意事项[J]. 石油技术监督,2005,21(11):12-14.
【12】刘卫东, 吕拴录, 韩勇,等. 特殊螺纹接头油、套管验收关键项目及影响因素[J]. 石油矿场机械, 2009, 38(12): 23-26.
【13】API RP 5C5-2003Recommended practice for eva-luation procedure for casing and tubing connection[S].
【2】吕拴录, 王震, 康延军, 等. 某气井完井管柱泄漏原因分析[J]. 油气井测试, 2010, 19(4): 58-60.
【3】张福祥,吕拴录,王振彪, 等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全, 2010,26(5): 65-68.
【4】吕拴录, 李元斌, 王振彪, 等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J]. 腐蚀与防护, 2010, 31(11): 902-904.
【5】LV Shuan-lu, LI Zhi-hou,HAN Yong. High dogleg severity,wear ruptures casing string[J]. Oil & Gas, 2004, 98(49): 74-80.
【6】许峰, 吕拴录, 康延军, 等. 井口套管磨损失效原因分析及预防措施研究[J]. 石油钻采工艺, 2011, 33(2): 140-142.
【7】LV Shuan-lu, TENG Xue-qing, KANG Yan-jun,et al. Analysis on causes of a well casing coupling crack[J]. Materials Performance, 2012,51(4):58-62.
【8】吕拴录, 李鹤林. V150套管接箍破裂原因分析[J]. 理化检验-物理分册,2005, 41(增1): 285-290.
【9】吕拴录, 张福祥, 李元斌, 等. 塔里木油气田非API油井管使用情况统计分析[J]. 石油矿场机械, 2009,38(7): 70-74.
【10】吕拴录, 韩勇. 特殊螺纹接头油、套管使用及展望[J]. 石油工业技术监督,2003(3):1-4.
【11】吕拴录. 特殊螺纹接头油套管选用注意事项[J]. 石油技术监督,2005,21(11):12-14.
【12】刘卫东, 吕拴录, 韩勇,等. 特殊螺纹接头油、套管验收关键项目及影响因素[J]. 石油矿场机械, 2009, 38(12): 23-26.
【13】API RP 5C5-2003Recommended practice for eva-luation procedure for casing and tubing connection[S].
相关信息