Residual Stress of Nuclear Power Rotor Wheel Disk and Blade Groove after Shot Peening Treatment
摘 要
对核电轮盘以及叶根槽采用喷丸强化处理, 利用X射线应力分析方法研究了轮盘喷丸后表面残余应力的均匀性, 以及轮盘、叶根槽喷丸试样的残余应力沿层深的分布规律。结果表明: 喷丸处理后轮盘表面残余应力分布均匀, 轮盘及叶根槽最大残余应力值分别达到 -667.9 MPa和-587.5 MPa。
Abstract
Nuclear power rotor wheel disk and blade groove were treated by shot peening. The uniformity of surface residual stress of rotor wheel sample and residual stress depth distribution of both wheel disk and blade groove were investigated by X-ray diffraction method. The results showed that the residual stress was well-distributed on the surface, meanwhile, the maximum residual stress for wheel disk and blade groove after shot peening reached -667.9 MPa and -587.5 MPa, respectively.
中图分类号 TG178
所属栏目 试验与研究
基金项目
收稿日期 2013/4/7
修改稿日期
网络出版日期
作者单位点击查看
备注袁建平(1965-), 男, 高级工程师。
引用该论文: YUAN Jian-ping,CHENG Gang,DING Li-feng,SHEN Ru-guo,WU Chun-dong. Residual Stress of Nuclear Power Rotor Wheel Disk and Blade Groove after Shot Peening Treatment[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(7): 427~428
袁建平,程钢,丁丽峰,申如国,吴春冬. 核电轮盘及叶根槽喷丸层的残余应力[J]. 理化检验-物理分册, 2013, 49(7): 427~428
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李光彦, 沙命余.汽轮机叶轮缘反T型叶根槽断裂的超声波探伤[J].无损检测, 1999,21(11):509-511.
【2】徐鲲濠, 王恒烽,李湘军,等.汽轮机末级叶片叶根的喷丸强化[J].机械工程材料, 2012,36(11): 79-101.
【3】王仁智.表面喷丸强化机制[J].机械工程材料, 1988, 68(5): 19-23.
【2】徐鲲濠, 王恒烽,李湘军,等.汽轮机末级叶片叶根的喷丸强化[J].机械工程材料, 2012,36(11): 79-101.
【3】王仁智.表面喷丸强化机制[J].机械工程材料, 1988, 68(5): 19-23.
相关信息