7A04模锻螺母开裂原因分析
Analysis on Cracking Cause of 7A04 Forging Nut
摘 要
通过化学成分分析、硬度测试、宏观及微观检验对某螺母螺纹根部出现开裂的原因进行了分析。结果表明: 螺母开裂的原因是其存在设计缺陷, 即退刀槽设计为模锻件的分模面, 致使关键部位螺纹根部存在非锻造组织而使强度弱化。
开裂
模锻
分模面
流线
nut
cracking
forging
parting surface
flow lines
Abstract
By means of chemical composition analysis, hardness testing, macro and micro examination, the cause of cracking in the thread roots of a nut was analyzed. The results showed that the cracking was due to the design flaw of nut, the undercut was designed for the parting surface of die forgings, resulting in non-forging organizations in the key parts of thread roots, and the strength was weakened.
中图分类号 V244.21+2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/3/26
修改稿日期
网络出版日期
作者单位点击查看
备注王文斌(1967-), 男, 高级工程师, 工学学士。
引用该论文: WANG Wen-bin. Analysis on Cracking Cause of 7A04 Forging Nut[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(7): 482～485
王文斌. 7A04模锻螺母开裂原因分析[J]. 理化检验－物理分册, 2013, 49(7): 482～485
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 3246.1～3246.2—2000变形铝及铝合金制品组织检验方法[S].
【2】丁惠麟,辛智华.实用铝、铜及其合金金相热处理和失效分析[M].北京: 机械工业出版社, 2007: 326-339.
【2】丁惠麟,辛智华.实用铝、铜及其合金金相热处理和失效分析[M].北京: 机械工业出版社, 2007: 326-339.
相关信息