储气球罐连接阀螺栓断裂分析
Fracture Analysis on Bolts Used for Valve of Gas-hold Spheric Tank
摘 要
储气球罐连接阀螺栓在使用过程中发生异常断裂。通过宏观观察、扫描电镜及能谱分析、金相检验等方法对螺栓断裂的原因进行了分析。结果表明: 螺栓在低应力及环境腐蚀性介质作用下发生了应力腐蚀开裂, 产生的原因是晶界析出较多高铬碳化物, 局部呈网络状, 使晶界贫铬, 导致了晶界的耐腐蚀性能下降。可以从改善环境条件及对材料进行稳定化处理等途径解决该问题。
螺栓
低应力脆断
应力腐蚀开裂
沿晶断裂
腐蚀坑
高铬碳化物
gas-hold spheric tank
bolt
low stress brittle fracture
stress corrosion cracking
intergranular fracture
corrosion pit
high chrome carbonide
Abstract
The bolts used for valve of gas-hold spheric tank were fractured abnormally in service. The fracture reason was analyzed by means of macroscopic observation, analysis by scanning electronic microscope and energy spectrum, metallographic examination and so on. The results showed that stress corrosion cracking was happened because of low stress and environmental corrosion. The cracking reason was that many high chrome carbonide precipitated at grain boundary which induced the reduction of chrome content and corrosion resistance of grain boundary. It could be solved by improving environmental condition and stabilizing treatment to the material.
中图分类号 TF764+.1 TH49
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/3/31
修改稿日期
网络出版日期
作者单位点击查看
备注张彦文(1972-), 男, 博士。
引用该论文: ZHANG Yan-wen,WU Li-xin,WANG Zhi-fen,TAO Yong. Fracture Analysis on Bolts Used for Valve of Gas-hold Spheric Tank[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(9): 628～631
张彦文,吴立新,王志奋,陶勇. 储气球罐连接阀螺栓断裂分析[J]. 理化检验－物理分册, 2013, 49(9): 628～631
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙智, 倪宏昕, 彭竹琴.现代钢铁材料及其工程应用[M]. 北京: 机械工业出版社, 2007.
【2】孙智, 江利, 应展鹏,等.失效分析——基础与应用[M].北京: 机械工业出版社, 2005.
【3】黄云群, 李明.反应器冷却水管失效分析与改进措施[J].理化检验-物理分册,2005,41(10): 524-539.
【4】廖景娱.金属构件失效分析[M].北京: 化学工业出版社, 2003.
【2】孙智, 江利, 应展鹏,等.失效分析——基础与应用[M].北京: 机械工业出版社, 2005.
【3】黄云群, 李明.反应器冷却水管失效分析与改进措施[J].理化检验-物理分册,2005,41(10): 524-539.
【4】廖景娱.金属构件失效分析[M].北京: 化学工业出版社, 2003.
相关信息